傅武兴,俞昊,陈彦模,黄涛,张瑜,朱美芳
FU Wu-xing,YU Hao,CHEN Yan-mo,HUANG Tao,ZHANG Yu,ZHU Mei-fang(State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

• 1:东华大学材料科学与工程学院纤维材料改性国家重点实验室

摘要(Abstract)：

以原位悬浮聚合法制备聚苯乙烯/超支化聚酰胺酯(PS/HBP)复合粒子,通过双螺杆共混挤出制备系列聚丙烯(PP)/PS/HBP三元共混物。运用傅里叶变换红外光谱仪对PS/HBP复合粒子进行分析,以偏光显微镜、差示扫描量热仪和锥板流变仪等仪器研究了PP/PS/HBP共混体系的相容性、聚集态结构、结晶性和流变性等性能,以万能材料试验机、红外染色机和电脑测色仪研究纤维的力学性能和染色性能。结果表明:PP、PS为热力学不相容体系,少量HBP的加入即可改变PP球晶结构,使球晶小而密,同时PS均匀分散在PP中;引入HBP使得PP的结晶结构有所完善,结晶温度和结晶度升高;引入PS/HBP复合粒子对PP纤维可纺性影响不大,表现为结构化黏度指数轻微升高,但共混纤维可拉伸性较纯PP有极大提高,力学性能有明显改善,染色性能也有显著提高。
Polystyrene/hyperbranched polyesteramide(PS/HBP) composite granules were synthesized by in-situ suspension polymerization technique.A twin-screw extruder was used to prepare the PP/PS/HBP ternary blend system.The ingredient of PS/HBP composite particles was characterized by Fourier transform infrared spectroscopy(FT-IR).The compatibility,aggregation structure,crystallinity and rheological behavior of the PP/PS/HBP ternary blend system were investigated by the polarization microscope(PLM),differential scanning calorimetry(DSC) and rotational rheometer,respectively.The mechanical property and dyeing property were characterized by universal material testing machine,infrared dyeing machine and computer color measurement instrument,respectively.The morphology of PP and PS showed that they were incompatible system,and PS distributed evenly in the spherocrystal of PP.The crystallization behavior of PP in PP/PS/HBP ternary blend system showed HBP acted as a nucleation agent which could dramatically destroy the spherocrystal of PP,while the degree of crystallinity and crystal perfection were improved with the increasing content of HBP.The rheology behavior of PP/PS/HBP blends was similar to that of PP.Mechanical and dyeable performance of PP fiber after-drawing process was significantly improved than that of neat PP.

关键词(KeyWords)： 聚丙烯;超支化聚酰胺酯;聚苯乙烯;力学性能;染色性能;悬浮聚合
polypropylene,hyperbranched polyesteramide,polystyrene,mechanical property,dyeing property,suspension polymerization

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 傅武兴,俞昊,陈彦模,黄涛,张瑜,朱美芳
FU Wu-xing,YU Hao,CHEN Yan-mo,HUANG Tao,ZHANG Yu,ZHU Mei-fang(State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

DOI: 10.16090/j.cnki.hcxw.2013.01.002

参考文献(References)：

• [1]李雪莲.聚丙烯纤维的发展[J].上海丝绸,2005(1):9-17.
• [2]张秀芹,高小山,朱本松.改性聚丙烯纤维的染色性[J].北京服装学院学报,2000,20(2):15-19.
• [3]马少君,于贵春,王玉芬,等.聚丙烯/凹凸棒土复合材料的结晶行为[J].合成纤维,2011,40(9):19-22.
• [4]花秀兵,张瑜,阎惠至,等.聚丙烯/聚苯乙烯/膨润土共混体系的结晶性能和热性能研究[J].合成纤维,2010,39(1):18-20.
• [5]Gang Xu,Wenfang Shi,Peng Hu,et al.Crystallization kinetics of polypropylene with hyperbranched polyurethane acrylate being used as a toughening agent[J].European Polymer Journal,2005,41(8):1828-1837.
• [6]A K Bledzki,O Faruk.Wood fibre reinforced polypropylene compos-ites:Effect of fibre geometry and coupling agent on physico-mechanical properties[J].Appl Compos Mater,2003,10(6):365-379.
• [7]M Biswal,S Mohanty,S K Nayak.Thermal stability and flammability of banana-fiber-reinforced polypropylene nanocomposites[J].Journal of Applied Polymer Science2012,125:432-443.
• [8]Sari Morteza Ganjaee,Moradian Siamak Bastani Saeed,et al.Modifi-cation of poly(propylene)by grafted polyester-amide-based dendritic nanostructures with the aim of improving its dyeability[J].Journal of Ap-plied Polymer Science2012,124(3):2449-2462.
• [9]秦艳华,刘丽君,夏英姿,等.用TPEE改善PP纤维染色性能的研究[J].合成纤维,2004,33(4):7-8.
• [10]X Huang,H Yu,M F Zhu,et al.Blends of polypropylene and modi-fied polystyrene for dyeable fibers[J].Journal of Applied Polymer Science,2005,96(6):2360-2366.
• [11]Q Xing,M F Zhu,Y H Wang,et al.In situ gradient nano-scale fib-ril formation during polypropylene(PP)/polystyrene(PS)composite fine fiber processing[J].Polymer,2005,46(14):5406-5416.
• [12]H Y Huo,H Z Yan,Y Zhang,et al.The thermal and mechanical properties of hyperbranched poly(ester-amide)/polypropylene blends[J].Donghua Univ Press:Shanghai,2009:668-671.
• [13]陆琰,朱美芳,黄欣,等.PP/PS共混体系相容性及共混纤维性能研究[J].高分子材料科学与工程,2001,17(2):95-98.
• [14]胡明,徐德增,郭静.超支化聚酰胺对聚丙烯及其纤维的性能影响[J].合成纤维工业,2007,30(4):30-33.
• [15]Z Bartczak,A Galeski,N P Krasnikova.Primary nucleation and spherulite growth rate in isotactic polyproplene-polystyrene blends[J].Polymer,1987,28(10):1627-1634.
• [16]沈新元.高分子材料加工原理.第2版.北京:中国纺织出版社.2009.
• [17]Miyazaki K,Tabata I,Hori T.Relationship between colour fastness and colour strength of polypropylene fabrics dyed in supercritical carbon dioxide:effect of chemical structure in1,4-bis(alkylamino)anthraquinone dyestuffs on dyeing performance[J].Color Technol,2012,128(1):60-67.