孟志芬,胡学超
MENG Zhi-fen1; HU Xue-chao2 (1.Henan Institute of Science and Technology;

• 1:河南科技学院
• 2:东华大学 新乡453003
• 3:上海200051

摘要(Abstract)：

采用DDV-II型粘弹谱仪对Lyocell纤维的动态力学性能进行了研究。实验结果表明:与粘胶纤维不同,Lyocell纤维的力学损耗正切─温度曲线有两个明显的力学吸收峰,包含两种不同的吸收机理,并且纺丝速度对Lyocell纤维的动态力学性能有一定的影响。
The dynam ic m echanicalproperty ofLyocellfiberw as studied by the dynam ic viscoelastic m ethod. The result showed that the dynamic loss tan!- T curves of Lyocell fiber had two peaks and included two types of viscoelastic absorption mechanism. This was different from the viscose fiber apparently.The spinning speed had some influence on the dynamic mechanical property.

关键词(KeyWords)： Lyocell纤维;动态力学性能;纺丝速度;粘弹性吸收机理
Lyocellfiber,dynam icm echanicalproperty,spinning speed,viscoelasticabsorption m echanism

Abstract:

Keywords:

基金项目(Foundation):

作者(Authors): 孟志芬,胡学超
MENG Zhi-fen1; HU Xue-chao2 (1.Henan Institute of Science and Technology;

参考文献(References)：

• [1]陈稀,黄象安.化学纤维实验教程.纺织工业出版社.1988.152.
• [2]孟志芬.中国纺织大学硕士研究生学位论文.1998.34￣46.
• [3]邵惠丽,段菊兰等.合成纤维.2000,29(3):3￣5.
• [4]段菊兰,邵惠丽等.合成纤维工业.1999,22(5):23￣24
• [5]W E Morton,J W S Hearle著.杨屏玉译.纤维加热时的结构变化.Physical Properties of Textile Fibers,1975,P9539￣9610.
• [6]上出健二,栗木登男等.ポリエチレンテレフタレ—ト纤维の粘弹性—温度特性から评价レた无定形领域超分子构造,纤维机械学会志,1995,38(5):85￣92.
• [7]真锅征一,上出健二等著.王依民译.与纤维和成纤高分子材料无定形区分子运动有关的力学损耗tanδ￣T曲线的分析,纤维机械学会志,1977,30(3):41￣50.