张世宇,赵伟,刘龙刚,李峰
ZHANG Shi-yu,ZHAO Wei,LIU Long-gang,LI Feng

• 1:西安交通工程学院土木工程学院
• 2:西北工业大学力学与土木建筑学院

摘要(Abstract)：

为了提高隧道用水泥土的力学性能，选择P.O 42.5硅酸盐水泥作为材料，掺入不同添加量和长度的聚乙烯醇(PVA)纤维，并进行拉伸强度试验。研究结果表明：当在水泥土中添加PVA纤维后，被拉试样先从最大强度快速减小至某一值，之后趋于相对稳定的状态；加入纤维后获得了更高的拉伸强度；PVA纤维/水泥土呈现塑性破坏的特点，拉伸性能并没有彻底失效，形成了一定残余强度。本研究开发的PVA纤维/水泥土加强了水泥土的综合性能，具有很好的应用价值。
In order to improve the mechanical properties of the tunnel cement, P.O 42.5 portland cement was selected as the material, and polyvinyl alcohol(PVA) fiber was mixed with different amount and length,and the tensile strength test was carried out. The research results show that when PVA fiber is added to the soil-cement, the stretched sample first decreases rapidly from the maximum strength to a certain value, and then tends to a relatively stable state. Higher tensile strength is obtained by adding fiber. The PVA fiber/soil-cement showed the characteristics of plastic failure, and the tensile properties don't fail completely,and a certain residual strength is formed. The PVA fiber/cement-soil developed in this study enhances the comprehensive properties of cement-soil and has good application value.

关键词(KeyWords)： 水泥土;聚乙烯醇纤维;拉伸强度
soil-cement;polyvinyl alcohol fiber;tensile strength

Abstract:

Keywords:

基金项目(Foundation): 陕西省教育厅一般性科研专项项目(20JK0748)

作者(Author): 张世宇,赵伟,刘龙刚,李峰
ZHANG Shi-yu,ZHAO Wei,LIU Long-gang,LI Feng

DOI: 10.16090/j.cnki.hcxw.2022.11.020

参考文献(References)：

• [1]夏香港,张经双,刘永翔.冻融循环下混杂纤维粉煤灰水泥土损伤劣化[J].中国科技论文, 2022, 17(4):413-417.
• [2]牛雷,徐丽娜,郑俊杰,等.多种因素对纤维水泥红土加固效果的影响[J].科学技术与工程, 2022, 22(10):4083-4089.
• [3]庄心善,寇强.海水腐蚀环境下纳米SiO2改良水泥土动应力及微观分析[J].水文地质工程地质, 2022, 49(2):86-93.
• [4]王正龙,邓杰,梅岭,等.聚乙烯醇纤维加筋水泥固化疏浚土静力特性试验研究[J].江苏科技大学学报(自然科学版), 2021, 35(4):104-108.
• [5]许永静,刘国平,王有富,等.以水为单一增塑剂的PVA纤维的制备及结构性能研究[J].合成纤维工业, 2020, 43(1):7-11.
• [6]王明学, MUHAMMAD F A,张华鹏,等. PVA纤维表面改性对水泥基复合材料弯曲性能的影响[J].合成纤维, 2019, 48(1):37-41+45.
• [7] LI J, TANG C S, WANG D Y, et al. Effect of discrete fibre reinforcement on soil tensile strength[J]. Journal of Rock Mechanics and Geotechnical Engineering, 2014, 6(2):133-137.
• [8]陈峰.玄武岩纤维水泥土抗拉性能试验研究[J].深圳大学学报(理工版), 2016, 33(2):188-193.
• [9] FESTUGATO L, ESTéFANO M, FERNANDA B, et al. Fibre-reinforced cemented soils compressive and tensile strength assessment as a function of filament length[J]. Geotextiles and Geomembranes, 2017, 45(1):77-82.
• [10]刘凤利,韦凯言,杨飞华,等.聚乙烯醇纤维改性EPS水泥土性能试验研究[J].功能材料, 2021, 52(12):12055-12060.
• [11]刘雁宁,张涛,李杉.混掺精细钢纤维/PVA纤维水泥基复合材料力学性能试验研究[J].混凝土, 2022(1):112-115.
• [12]魏发云,杨帆,王海楼,等.改性聚乙烯醇纤维增强水泥基复合材料制备及其力学性能[J].纺织学报, 2021, 42(10):53-60.