竹原纤维与丙烯酸酯接枝物的结构与性能研究Study on the Structure and Properties of Bamboo Fiber Grafted with Acrylate
刘燕平,吴济宏,陈小燕
LIU Yan-ping, WU Ji-hong, CHEN Xiao-yan (Wuhan University of Science & Engineering
摘要(Abstract)：
以Ce4+引发丙烯酸甲酯(MA)、丙烯酸乙酯(EA)、丙烯酸丁酯(BA)与竹原纤维进行接枝聚合,用ATR、SEM、XRD和TG等手段表征接枝纤维的结构。接枝后纤维强度和初始模量下降,断裂伸长和柔顺性提高;耐酸、耐碱能力随接枝率的增加而提高,热稳定性提高,回潮率下降。接枝单体对纤维的改性效果顺序为BA>EA>MA。
Graft copolymerizations of methyl acrylate (MA), ethyl acrylate (EA) and butyl acrylate (BA) onto bamboo fiber using Ce4+ as initiator were introduced. The structure of grafted products was characterized by means of ATR, SEM, X-ray diffraction and TG. The tensile strength and initial modulus were remarkably decreased and the breaking elongation and flexibility of grafted fiber were increased. As the grafting yield increased the acid and base resistance of grafted fiber were increased, and the thermal stability were also increased, but the moisture regain were decreased. The best effect of modification was doing with BA, and the followings were EA、MA.
关键词(KeyWords)：
竹原纤维;丙烯酸酯;接枝共聚;初始模量;刚度
bamboo fiber, acrylate, graft copolymerization, initial modulus, rigidity
基金项目(Foundation):
作者(Author):
刘燕平,吴济宏,陈小燕
LIU Yan-ping, WU Ji-hong, CHEN Xiao-yan (Wuhan University of Science & Engineering
参考文献(References)：
- [1]Princi E,Vicini S,et al.Thermal analysis and characterisation of cel-lulose grafted with acrylic monomers[J].Thermochim Acta,2005,425(1-2):173-179.
- [2]Princi E,Vicini S,et al.Grafting polymerization on cellulose based textiles:a13C solid state NMR characterization[J].European Polymer Journal,2005,41(6):1196-1203.
- [3]Princi E,Vicini S,et al.Synthesis and mechanical characterisation of cellulose based textiles grafted with acrylic monomers[J].European Poly-mer Journal,2006,42(1):51-60.
- [4]巫拱生,雷新建,吴兴久.甲基丙烯酸甲酯及丙烯酸乙酯与麻类纤维接枝共聚反应规律[J].吉林大学自然科学学报,1988,(1):107-111.
- [5]Karlsson J O,Gatenholm P.Solid-supported wettable hydrogels pre-pared by ozone induced grafting[J].Polymer,1996,37(19):4251-4256.
- [6]Karlsson J O,Gatenholm P.Preparation and characterization of cellu-lose-supported HEMA hydrogels[J].Polymer,1997,38(18):4727-4731.
- [7]Karlsson J O,Gatenholm P.Cellulose fibre-supported pH-sensitive hydrogels[J].Polymer,1999,40(2):379-387.
- [8]Karlsson J O,Andersson A,et al.Swelling behavior of stimuli-re-sponsive cellulose fibers[J].Polymer,1998,39(16):3589-3595.
- [9]Khan F,Ahnad S R.Graft copolymerization reaction of water emulsi-fied methyl methacrylate with pre-irradiated jute fibers[J].Journal of Ap-plied Polymer Science,1997,65(3):459-468.
- [10]George J,Bhagawan S S,Thomas S.Thermogravimetric and dynamic mechanical thermal analysis of pineapple fibre reinforced polyethylene composites[J].Journal of Thermal Analysis and Calorimetry,1996,47(4):1121-1140.