用两种环氧树脂上浆剂对国产聚丙烯腈基碳纤维进行上浆,测试和比较了两种环氧树脂上浆剂对聚丙烯腈(PAN)基碳纤维耐磨性、与水接触角、表面能等性能以及拉伸强度、伸长率、层间剪切强度(ILSS)等力学性能的影响。上浆剂中主体成分环氧树脂相对分子质量不是影响碳纤维层间剪切强度的决定性因素。
Two kinds of domestic sizing agents for PAN-based carbon fiber(CF) were comparatively studied on the physical properties such as wear resistance,contact angle,surface energy and mechanical properties of tensile strength,elastic modulus,interlaminar shear strength(ILSS).The effect of drying temperature on the water content of CF was also followed.The molecular weight of epoxy resin in sizing agent was not main influencing factor on interlaminar shear strength of carbon fiber.

关键词(KeyWords)： 聚丙烯腈纤维;碳纤维;上浆剂;环氧树脂
polyacrylonitrile fiber,carbon fiber,sizing agent,epoxy resin

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 张永刚,王雪飞,钱鑫,陈礼群,杨建行
ZHANG Yong-gang,WANG Xue-fei,QIAN Xin,CHEN Li-qun,YANG Jian-xing(State Engineering Laboratory for Carbon Fiber Preparation

DOI: 10.16090/j.cnki.hcxw.2011.12.001

参考文献(References)：

• [1]贺福.碳纤维及石墨纤维[M].北京:化学工业出版社,2010.
• [2]张晓虎,孟宇,张炜.碳纤维增强复合材料技术发展现状及趋势[J].纤维复合材料,2004(1):50-58.
• [3]Broyles N S.Sizing of carbon fibres with aqueous solutions of poly(vinyl pyrollidone)[J].Polymer,1998,39(12):2 607-2 613.
• [4]王学兰,曾黎明.碳纤维上浆剂的研究进展[J].炭素技术,2011,30(2):26-29.
• [5]李伟东,王岭,王云英,等.上浆剂对国产碳纤维/聚酰亚胺复合材料界面性能的影响[J].失效分析与预防,2010,5(3):135-139.
• [6]李阳,温月芳,杨永岗,等.环氧树脂上浆剂对PAN基碳纤维性能的影响[J].合成纤维工业,2009,32(2):1-3.
• [7]肇研,段跃新.上浆对碳纤维表面性能的影响[J].材料工程,2007,(Z1):121-126.
• [8]Park J M,Kim D S,Kim S R.Improvement of interfacial adhesionand nondestructive damage evaluation for plasma-treated PBO andKevlar fibers/epoxy composites using micromechanical techniques andsurface wettability[J].Journal of Colloid and Interface Science,2003,264:431-445.
• [9]Cantin S,Boutesu M,Benhabib F,et al.Surface free energyevaluation of well-ordered Langmuir-Blodgett surfaces Comparison ofdifferent approaches[J].Colloids and surfaces A:Physicochem EngAspects,2006,276:107-115.
• [10]马全胜,李敏,孙志杰,等.固化阶段环氧树脂表面能及其极性变化的表征[J].复合材料学报,2009,26(5):74-79.
• [11]Cheng T H,Zhang J,Yumitor,et al.Sizing resin structure andinterphase formation in carbon fibre composites[J].Composites,1994,25(7):661-670.
• [12]余奇平,滕翠青,余木火.国内外碳纤维上浆剂研究现状[J].纤维复合材料,1997(2):50-54.