P34HB共混改性聚乳酸纤维柔软性能研究P34HB Blending Modification of Polylactic Acid Fiber for Better Softness
曾方,何娇,何洪林,黄胤宁
ZENG Fang,HE Jiao,HE Hong-lin,HUANG Yin-ning
摘要(Abstract)：
将聚乳酸与聚3-羟基丁酸酯-4-羟基丁酸酯共聚物(P34HB)按一定比例进行共混,再用熔融纺丝的方法制备聚乳酸共混纤维,通过扫描电镜、X射线衍射仪、织物风格仪等对纤维的结晶取向、相容性、力学性能、手感等进行了研究。结果表明:随着P34HB含量增加,共混纤维的断裂强度下降,断裂伸长率变大,分子链的取向度、动态弹性模量降低;但P34HB的加入,能大大改善织物的表面粗糙度,特别在P34HB质量分数为40%的时候,共混织物表面粗糙度为3.07μm,表面光滑;并且该比例的织物易剪切变形,剪切回复力好,能轻松错动。
The polylactic acid and poly-3-hydroxybutyrate 4-hydroxybutyrate copolymer(P34HB) were blended in a certain percentage, and then polylactic acid blended fibers was prepared by melt spinning. Fiber crystal orientation, compatibility, mechanical property, softness and so on were investigated by SEM,XRD, fabric style instrument etc. It is concluded that as P34HB content increases, tensile strength of blended fiber decreases, elongation becomes larger, the degree of orientation of molecular chains, dynamic Young's modulus decrease. However, with the addition of P34HB, the surface roughness of the fabric greatly improves, especially in 40% P34HB content. The blended fabric surface roughness is 3.07 μm, fiber hassmooth surface and good shear restoring force, easy to deform and dislocate.
关键词(KeyWords)：
聚乳酸纤维;聚3-羟基丁酸酯4-羟基丁酸酯共聚物;共混改性;手感
polylactic acid fiber;poly-3-hydroxybutyrate-4-hydroxybutyrate copolymer;blending modification;softness
基金项目(Foundation):
作者(Author):
曾方,何娇,何洪林,黄胤宁
ZENG Fang,HE Jiao,HE Hong-lin,HUANG Yin-ning
DOI: 10.16090/j.cnki.hcxw.2019.12.004
参考文献(References)：
- [1]潘招银,蔡培展.聚乳酸:让微生物降解塑料[J].广州化工, 2019, 47(5):11-12.
- [2]林海娟,方建勇,董丽松.聚乳酸阻燃性能的研究进展[J].高分子通报, 2012(3):45-52.
- [3]沈鑫,刘雪,宿烽,等.完全可降解聚乳酸及其共聚物的生物相容性:研究、应用与未来[J].中国组织工程研究, 2018, 22(14):2259-2264.
- [4] XU X, YANG Q, WANG Y, et al. Biodegradable electrospun poly(Llactide)fibers containing antibacterial silver nanoparticles[J]. European Polymer Journal, 2006, 42(9):2081-2087.
- [5]张巍峰.聚乳酸纤维染色性能的研究[J].染整技术, 2019, 41(3):20-23.
- [6] SCHEYER L E, CHIWESHE A. Application and performance of disperse dyes on polylactic acid(PLA)fabric[J]. AATCC Review, 2001(1):44-48.
- [7]韩露,马芳武,陈实现,等.玄武岩纤维增强聚乳酸力学性能及耐老化性能[J].化工学报, 2019, 70(3):1171-1178.
- [8] AVEROUS L, BOQUILLON N. Biocomposites based on plasticized starch:thermal and mechanical behaviours[J]. Carbohydrate Polymers,2004, 56(2):111-122.
- [9] AVINC O, KHODDAMI A. Overview of poly(lactic acid)(PLA)fibre[J]. Fibre Chemistry, 2010, 42(1):68-78.
- [10] SANJEEV Singh, AMAR K Mohanty, TOMOHIKO Sugie, et al. Renewable resource based biocomposites from natural fiber and polyhydroxybutyrate-co-valerate(PHBV)bioplastic[J]. Composites Part A, 2008, 39(5).