崔华帅,史贤宁,吴鹏飞,崔宁
CUI Hua-shuai,SHI Xian-ning,WU Peng-fei,CUI Ning

• 1:中国纺织科学研究院

摘要(Abstract)：

以聚苯硫醚(PPS)树脂和聚对苯二甲酸乙二醇酯(PET)树脂为原料,采用复合纺丝技术,制得PPS-PET皮芯复合纤维。对纯PPS纤维和PPS-PET复合纤维分别进行了紫外线照射、热处理和耐酸碱处理,对比了两者处理后的力学性能变化,验证了复合纤维应用的可行性。试验结果表明:PPS-PET皮芯复合纤维的耐热性能略低于PPS纤维;而经过同等强度的紫外光辐照后,PPS-PET皮芯复合纤维的强度保持率是PPS纤维的2倍左右;在试验条件下经过酸、碱浸泡后,PPS-PET皮芯复合纤维的强度保持率与PPS纤维相比未表现出明显差异。性能研究结果表明:通过复合纺丝,PPS纤维的综合性能有所改善。
PPS-PET core-sheath composite fiber was prepared by composite spinning with poly(phenylenesulfide) and poly(ethyelene terephthalate) as the raw materials. The influences of ultraviolet radiation, heatexposure and acid&alkali treatment on the fiber were studied. Mechanical properties of the fiber before andafter the treatments had been compared to confirm the feasibility of the fiber's application. The researchshowed that the heat resistant property of the composite fiber was slightly lower that than of PPS fiber, afterbeing exposed to same concentration of ultraviolet, the strength retention of the composite fiber was 2 timesof PPS fiber, after being separately soaked in certain condition of acid solution and alkali solution, nodistinct difference had been detected about the strength retention between composite fiber and PPS fiber.The research showed that the overall properties of the fiber had been improved by the way of compositespinning.

关键词(KeyWords)： 聚苯硫醚;聚酯;皮芯复合纤维;酸碱;热处理;紫外线;强度
poly(phenylene sulfide);poly(ethyelene terephthalate);core-sheath composite fiber;acid and alkali;heat treatment;ultraviolet;strength

Abstract:

Keywords:

基金项目(Foundation): 国家科技支撑计划资助项目(2015BAE01B04)

作者(Author): 崔华帅,史贤宁,吴鹏飞,崔宁
CUI Hua-shuai,SHI Xian-ning,WU Peng-fei,CUI Ning

DOI: 10.16090/j.cnki.hcxw.2017.04.013

参考文献(References)：

• [1]王桦,覃俊,陈丽萍.聚苯硫醚纤维及其应用[J].合成纤维,2012,41(3):7-12.
• [2]曾红霞,肖哲.PP/PA6复合超细纤维的研制[J].合成纤维工业,2001,24(2):22-23.