王雪新,胡祖明,于俊荣,诸静,王彦
WANG Xue-xin,HU Zu-ming,YU Jun-rong,ZHU Jing,WANG Yan

• 1:东华大学纤维材料改性国家重点实验室东华大学材料科学与工程学院

摘要(Abstract)：

采用凝胶纺丝制备了氧化石墨烯(GO)改性的高强聚乙烯醇(PVA)纤维,研究了GO的含量、纺丝工艺对GO-PVA纤维性能的影响。通过红外光谱、热失重和热失重速率、差示扫描分析、X射线衍射等方法对GO-PVA纤维的结构与性能进行了研究。结果表明:GO-PVA纤维具有更好的拉伸性能,当GO质量分数在0.1%的时候,GO-PVA纤维具有最好的拉伸性能,其最大拉伸倍数、强度和模量分别为41倍、15.6 c N/dtex和185 c N/dtex,比纯PVA纤维提高了36.7%、16.4%和79.6%。
High strength polyvinyl alcohol(PVA) fiber was modified with graphene oxide(GO) and was prepared by gel spinning.The content of GO and gel spinning process were investigated.The structure and properties were investigated by SEM,FTIR,DSC,TG,DTG and XRD analysis.The results showed that the modified fiber had better tensile properties.When the content of GO was 0.1%,the properties of the GO-PVA fiber were the best,the maximum draw ratio,the tensile strength and modulus reached 41,15.6 cN/dtex and 185 cN/dtex,which compared with neat PVA fiber,increased by 36.7%,16.4%and 79.6%,respectively.

关键词(KeyWords)： 聚乙烯醇;高强高模纤维;氧化石墨烯;凝胶纺丝;改性
polyvinyl alcohol;high strength and high modulus fiber;graphene oxide;gel spinning;modification

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 王雪新,胡祖明,于俊荣,诸静,王彦
WANG Xue-xin,HU Zu-ming,YU Jun-rong,ZHU Jing,WANG Yan

DOI: 10.16090/j.cnki.hcxw.2016.06.003

参考文献(References)：

• [1]黄平.高强高模聚乙烯醇纤维的研究进展[J].合成纤维工业,2006,24(5):26-30.
• [2]李明星,王凯.高强高模聚乙烯醇(PVA)纤维的研究进展[J].合成纤维,2004,32(1):21-23.
• [3]纪俊祥,徐建军,张宇峰,等.一种高强高模聚乙烯醇纤维的制备方法:CN104328511A[P].2015.
• [4]GU J Y,JOO S E,JAE L Y,et al.Effect of gel spinning accompanied with cross-linking using boric acid on the structure an properties of high-molecular-weight poly(vinyl alcohol)Fiber[J].Journal of Applied Polymer Science,2009,113(3):1733-1738.
• [5]YAMAURA K,KUMAKURA R.Gelspinning of partially saponificated poly(vinyl alcohol)[J].Journal of Applied Polymer Science,2000,77(13):2872-2876.
• [6]俞波,刘兆峰,诸静,等.聚乙烯醇冻胶纺丝研究——凝固浴条件对纤维结构性能的影响[J].中国纺织大学学报,1993(6):55-61.
• [7]彭志勤,章倩,章悦庭,等.纳米无机晶须改性聚乙烯醇纤维的研究[J].维纶通讯,2005(4):16-18.
• [8]LU L,HOU W,SUN J,et al.Preparation of poly(vinyl alcohol)fibers strengthened using multiwalled carbon nanotubes functionalized with tea polyphenols[J].Journal of Materials Science,2014,49(9):3322-3330.
• [9]FU C,GU L.Composite fibers from poly(vinyl alcohol)and poly(vinyl alcohol)-functionalized multiwalled carbon nanotubes[J].Journal of Applied Polymer Science,2013,128(2):1044-1053.
• [10]XU X,Uddin A J,Aoki K,et al.Fabrication of high strength PVA/SWCNT composite fibers by gel spinning[J].Carbon,2010,48(7):1977-1984.
• [11]李亚平,王平华,刘春华,等.高强度聚乙烯醇/氧化石墨烯复合水凝胶[J].高分子材料科学与工程,2015(6):161-166.
• [12]CHEN J,LI Y,ZHANG Y,et al.Preparation and characterization of graphene oxide reinforced PVA film with boric acid as crosslinker[J].Journal of Applied Polymer Science,2015,132(22):1-8.
• [13]毕朝刚.氧化石墨烯及其复合物的制备与表征[D].大连:大连理工大学,2014:13.
• [14]马国富,李佳佳,彭辉,等.层状聚乙烯醇/氧化石墨烯纳米复合膜的制备及性能研究[J].西北师范大学学报:自然科学版,2013(6):63-67.
• [15]李佳佳.聚乙烯醇复合材料的制备及其性能研究[D].兰州:西北师范大学,2014:37.
• [16]白炳莲,韦珏,王海涛,等.用红外光谱技术研究氢键的键合方式[J].化学通报,2013,76(2):167-170.