胡培贤,温月芳,杨永岗,刘朗
HU Pei-xian1,2, WEN Yue-fang1, YANG Yong-gang*1

• 1:中国科学院山西煤炭化学研究所
• 2:中国科学院炭材料重点实验室

摘要(Abstract)：

常压下,使碳纤维通过以氨气为气体介质的600℃热反应炉,反应停留时间为30s。采用三点短梁法和界面评价装置研究处理前后复合材料的层间剪切强度(ILSS)和界面剪切强度(IFSS),经氨气处理后二者分别提高了13.2%和32.1%。接触角测试结果表明:处理后碳纤维与水和环氧树脂的浸润性得到很大改善。采用扫描电子显微镜(SEM)研究处理前后碳纤维表面和复合材料断裂面形貌的变化,发现氨气处理对碳纤维表面形貌没有影响。力学性能测试数据表明,氨气处理不影响碳纤维的强度。
The carbon fibers (CFs) were treated for 30 s at 600 ℃ under the normal pressure of the NH3 gas in the thermal furnace. After treated by NH3, the interlaminar shear strength (ILSS) and the interfacial shear strength (IFSS) of CF-reinforced resin composites (CFRP) increased by 13.2 % and 32.1 % respectively, found by three-point-bending approach and the equipment for fiber/resin composite interface properties evaluation. The contact angles of CFs indicated that the soack of CFs were remarkably improved in water or epoxy resin solution. The surface of CFs and the fractured surfaces of CFRP were studied by scanning electron microscope (SEM). The surface of CFs treated by free ammonia had no change compared with that of the untreated CFs. The mechanical analysis showed no effect on strength of CFs after treated by free ammonia.

关键词(KeyWords)： 碳纤维;氨气;表面处理;复合材料
carbon fiber, free ammonia, surface treatments, polymer-matrix composites

Abstract:

Keywords:

基金项目(Foundation): 973项目(项目编号:2006CB605304);; 国家自然科学基金项目(项目编号:50604025)

作者(Author): 胡培贤,温月芳,杨永岗,刘朗
HU Pei-xian1,2, WEN Yue-fang1, YANG Yong-gang*1

参考文献(References)：

• [1]Peter A Thrower.Chemistry and physics of carbon(18)[M].New York:Marcel dekker Inc,1982:95-97.
• [2]Z R Yue,W Jiang,L Wang,et al.Surface characterization of electro-chemically oxidized carbon fibers[J].Carbon,1999,37(11):1785-1796.
• [3]Y D Huang,L Liu,et al.Influence of ultrasonic treatment on thecharacteristics of epoxy resin and the interfacial property of its carbon fiber composites[J].Composites Science and Technology,2002,62(16):2153-2159.
• [4]M A Montes-Mora′n,et al.A study of the effect of plasma treatment on the interfacial properties of carbon fibre-thermoplastic composites[J].Carbon,2005,43(8):1778-1814.
• [5]刘鸿鹏,吕春祥,李永红等.电化学表面处理PAN基碳纤维的表面性能研究[J].新型碳材料,2005,20(1):39-44.
• [6]满华元,王鉴,余宗森.阳极氧化表面处理对碳纤维性能的影响[J].复合材料学报.1993,10(10):97-102.
• [7]冀克俭,邓卫华,陈刚等.臭氧处理对碳纤维表面及其复合材料性能的影响[J].工程塑料应用,2003,3l(5):34-36.
• [8]杜慷慨,林志勇.碳纤维表面氧化的研究.华侨大学学报(自然科学版)[J].1999,20(2):136-141.
• [9]杨永岗,贺福,王茂章等.高温空气氧化对炭纤维力学性能的影响[J].炭素技术,1997,6:12-14.
• [10]胡培贤,温月芳,杨永岗等.氨气处理碳纤维第I报表面组成和反应机理[J].合成纤维.2008,37(6):9-12.
• [11]Yonggang Yang,Fu He,Maozhang Wang,et al.A new surface treatment method of carbon fiber-liquid-phase-gas-phase double effec-tiveness method(LGDE)[J].Journal of materials science,1998,33:3651-3654.
• [12]杨永岗,贺福,王茂章等.碳纤维表面处理的新方法-气液双效法[J].材料研究学报,1998,12(2):207-208.
• [13]关蓉波.碳纤维上浆剂的研究[D].太原:中国科学院山西煤碳化学研究所,2002.
• [14]曹霞,温月芳,张寿春等.耐温型碳纤维乳液上浆剂[J].新型碳材料,2006,21(4):337-342.
• [15]王国建,郭建龙,屈泽华.乙二胺修饰的碳纳米管对环氧树脂力学性能的影响[J].玻璃钢/复合材料,2006,6:16-19.
• [16]曹春华,李家麟,贾志杰.用二胺在碳纳米管上引入胺基团的研究[J].新型炭材料,2004,19(2):137-140.