Lyocell-炭黑复合纤维的结构与性能Preparation and Properties of Lyocell-Carbon Black Composite Fibers
鲁江,张华山
LU Jiang,ZHANG Hua-shan
摘要(Abstract)：
将纳米炭黑、N-甲基吗啉-N-氧化物(NMMO)溶液及纤维素共混得到纺丝液,通过干湿法制备了Lyocell-炭黑复合纤维。采用X射线衍射仪、扫描电镜、强度仪等分析了所得纤维的结构和性能。X射线衍射图谱显示复合纤维仍然具有纤维素II晶型的结构,同时还保留了炭黑的特征衍射峰。扫描电镜结果显示复合纤维中炭黑在纤维素基体中有一些团聚。对纤维的力学性能及电导率分析进一步表明:添加炭黑使得复合纤维的初始模量和断裂强度下降,但是可以在一定程度上提高复合纤维的电导率。
Lyocell-carbon black composite fibers were prepared by the dry-wet spinning of carbon black,N-methylmorpholine N-oxide and the cellulose. WAXD, SEM and the tensile testing etc. were used to characterize the structure and properties of the composite fibers. WAXD pictures showed the composite fibers had the cellulose II crystal structure and retained the characteristic peak of carbon black. The SEM showed some carbon blacks were agglomerated in the matrix. The initial modulus and tenacity of the composite fibers were decreased with the addition of the carbon black dramatically, but the conductivity of the composite fiber was improved with the carbon black addition.
关键词(KeyWords)：
Lyocell纤维;炭黑;性能
Lyocell fiber;carbon black;property
基金项目(Foundation):
作者(Author):
鲁江,张华山
LU Jiang,ZHANG Hua-shan
DOI: 10.16090/j.cnki.hcxw.2013.11.024
参考文献(References)：
- [1]蔡剑.低温多效蒸发组合蒸汽喷射热压缩系统用于NMMO回收[J].合成纤维,2013,42(6):14-17.
- [2]付兰香.再生纤维素纤维的可持续发展方向[J].山东纺织科技,2000(5):51-54.
- [3]Vorbach D,Taeger E.含碳纤维素纤维的性能[J].国际纺织导报,1998(2):9-12.
- [4]Iijima S.Helical microtubules of graphitic carbon[J].Nature,1991,354:56-58.
- [5]Ruan S L,Gao P,Yu T X.Ultra-strong gel-spun UHMWPE fibers reinforced using multiwalled carbon nanotubes[J].Polymer,2006,47(5):1 604-1 611.
- [6]Zou Y B,Feng Y C,Wang L,et al.Processing and properties of MWNTs/HDPE composites[J].Carbon,2004,42(2):271-277.
- [7]Vorbach D,Taeger E.Properties of carbon filled cellulose filaments[J].Chemical Fibers International,1998,48(2):120-122.
- [8]Zhang H H,Guo L W,Shao H L,et al.Study on carbon black filled Lyocell fibers as the precursor of carbon fibers[J].Journal of Applied Polymer Science,2006,99(1):65-74.
- [9]刘新海,赵莹,刘智,等.改性纳米炭黑/聚氨酯复合物的制备及表征[J].高等学校化学学报,2008,29(10):2 096-2 100.
- [10]鲁江,简义辉,张慧慧,等.Lyocell/多壁碳纳米管复合纤维的制备及性能[J].新型炭材料,2007,22(2):159-164.
- [11]孙福,张国庆,孙艳秋.导电炭黑/聚酯复合材料的性能[J].纺织学报,2008,29(10):9-16.