田永龙,郭腊梅
TIAN Yong-long,GUO La-mei

• 1:东华大学产业用纺织品教育部工程研究中心东华大学纺织学院

摘要(Abstract)：

制备马来酸酐/苯乙烯接枝聚乙烯蜡(PEW-g-MAH/St),并使用其对UHMWPE纤维进行涂层改性处理,以提高纤维与树脂基体的界面黏接强度。分别研究与分析了MAH接枝率以及纤维拔出强度的影响因素。结果表明:随着马来酸酐(MAH)用量的增加,MAH接枝率随之逐渐增加;随着苯乙烯(St)用量的增加,MAH接枝率呈先增加后保持不变的趋势;红外分析表明MAH与St已被成功接枝到PEW大分子上;改性处理前后纤维的拉伸性能和结晶性能没有发生明显变化,但纤维的拔出强度和浸润性得到显著改善。
The maleic anhydride/styrene grafted polyethylene wax(PEW-g-MAH/St) was prepared, and the UHMWPE fiber was coated with it to improve the interfacial bonding strength between fiber and resin matrix. The factors affecting the grafting rate of MAH and the pull-out strength of fiber were studied and analyzed. The results showed that the grafting rate of MAH increased with the increase of MAH dosage. With the increase of St dosage, the grafting rate of MAH showed a trend of increasing first and then remaining unchanged. Infrared analysis showed that MAH and St had been successfully grafted onto PEW macromolecules. The tensile properties and crystallization properties of fiber did not change significantly before and after modification, but the pull-out strength and wettability of fiber were improved significantly.

关键词(KeyWords)： 超高相对分子质量聚乙烯纤维;PEW-g-MAH/St;界面黏接强度;浸润性
UHMWPE fiber;PEW-g-MAH/St;interfacial bonding strength;wettability

Abstract:

Keywords:

基金项目(Foundation): 中央高校基本科研业务费专项资金资助项目(102552016011)

作者(Author): 田永龙,郭腊梅
TIAN Yong-long,GUO La-mei

DOI: 10.16090/j.cnki.hcxw.2020.06.010

参考文献(References)：

• [1] KROMM F X, LORRIOT T, COUTAND B, et al. Tensile and creep properties of ultra high molecular weight PE fibres[J]. Polymer Testing,2003, 22(4):463-470.
• [2]孟祥雨,孙飞,杨军杰,等.高性能纤维的发展现状及特点与应用[J].合成纤维, 2014, 43(5):14-17.
• [3] OGAWA T, MUKI H, OSAWA S. Improvement of the mechanical properties of an ultrahigh molecular weight polyethylene fiber/epoxy composite by corona-discharge treatment[J]. Journal of Applied Polymer Science,2001, 79(7):1162-1163.
• [4]刘晓巧,张琳玫,孟家光,等. UHMWPE纤维针织物-环氧树脂复合材料的制备与性能[J].合成纤维, 2016, 45(3):35-37.
• [5] MURAOKA Y, RICH M J, DRZAL L T. Sulfonation of UHMW-PE fibers for adhesion promotion in epoxy polymers[J]. Journal of Adhesion Science and Technology, 2002, 16(12):1669-1685.
• [6] KUSANO Y, TEODORU S, HANSEN C M. The physical and chemical properties of plasma treated ultra-high-molecular-weight polyethylene fibers[J]. Surface&Coatings Technology, 2011, 205(8-9):2793-2798.
• [7]刘晓巧,孟家光,田萌.超高分子量聚乙烯纤维的低温等离子体处理[J].合成纤维, 2015, 44(10):25-29.
• [8] BROUJERDI M S, MASOOMI M, ASGARI M. Interfacial improvement and mechanical properties of epoxy resin/ultra-high molecular weight polyethylene fibre composites compatibilized with glycidyl methacrylate[J]. Journal of Reinforced Plastics and Composites, 2013, 32(22):1675-1684.
• [9] ZHU D, WANG Y, ZHANG X, et al. Interfacial bond property of UHMWPE composite[J]. Polymer Bulletin, 2010, 65(1):35-44.
• [10]王鉴,赵晶,祝宝东,等.溶液浸渍法协助二单体接枝改性聚乙烯[J].塑料, 2012, 41(4):79-81.
• [11]王瑾,曹贤武,梁健飞,等.反应挤出苯乙烯接枝改性聚烯烃热塑性弹性体的研究[J].塑料工业, 2018, 46(8):47-50.
• [12] AN M, XU H, LV Y, et al. Ultra-strong gel-spun ultra-high molecular weight polyethylene fibers filled with chitin nanocrystals[J]. RSC Advances, 2016, 6:20629-20636.