低温等离子体对国产聚酰亚胺纤维的亲水性改性研究Study on Hydrophilic Modification of Domestic Polyimide Fiber by Low-Temperature Plasma
孙依冉,杨建忠
SUN Yi-ran,YANG Jian-zhong
摘要(Abstract)：
采用低温等离子体改性技术,对国产聚酰亚胺纤维进行表面改性,从而提高了国产聚酰亚胺纤维的润湿性。对改性后的聚酰亚胺纤维进行表面形貌、表面化学结构、纤维力学性能、纤维静态水接触角以及束纤维芯吸效应的测试与分析,得知低温等离子体改性可以对国产聚酰亚胺纤维的表面进行刻蚀,使光滑的纤维表面出现凹槽,同时可以引入大量的亲水性官能团,提升纤维亲水性。当放电功率为130 W、放电时间为240 s、放电压强为25 Pa时,聚酰亚胺纤维的亲水性得到较大的改善,同时强力损失相对较小。
The low-temperature plasma modification technology was used to modify the surface of the domestic polyimide fiber to improve the wettability of the domestic polyimide fiber. The surface morphology,surface chemical structure, fiber mechanical property, fiber static water contact angle and bundle fiber wicking effect of the modified polyimide fiber were measured and analyzed. It is found that low-temperature plasma modification can etch the surface of domestic polyimide fiber to make grooves appear on the surface of smooth polyimide fiber, and a large number of hydrophilic functional groups can be introduced to improve the hydrophilicity of the fiber. When the discharge power is 130 W, the discharge time is 240 s and the discharge pressure is 25 Pa, the hydrophicity of polyimide fiber is improved the most, and the strenth loss is relatively small.
关键词(KeyWords)：
聚酰亚胺纤维;低温等离子体;亲水性
polyimide fiber;low-temperature plasma;hydrophilic
基金项目(Foundation): 陕西省科技厅重点研发计划项目(2019SF-232)
作者(Author):
孙依冉,杨建忠
SUN Yi-ran,YANG Jian-zhong
DOI: 10.16090/j.cnki.hcxw.2020.04.010
参考文献(References)：
- [1] DANG H Y, ZHANG X, LONG Z, et al. Ecofriendly preparation of cellulose nanocrystal-coated polyimide fiber:strategy for improved wettability[J]. Langmuir:the ACS Journal of Surfaces and Colloids, 2019, 35(33):10890-10899.
- [2]王倩倩,周燕萍,郑会保,等.耐高温聚酰亚胺树脂及其复合材料的研究及应用[J].工程塑料应用, 2019, 47(8):144-147.
- [3]王新华,徐旻.国产聚酰亚胺纤维性能及其纱线生产[J].棉纺织技术, 2018, 46(5):33-36.
- [4]吴谦,王栋,孙瑾.高性能纤维研究进展[J].化学工程师, 2013, 27(9):48-49, 66.
- [5]陈平,于祺,熊需海,等.高性能纤维表面改性及其双马树脂基复合材料界面[J].高分子学报, 2018(3):323-335.
- [6] SENER U, PAREKH B, ENTENBERG A, etc. Surface modification of poly(biphenyl dianhydride-para-phenylene diamine)(BPDA-PDA)polyimide by UV photo-oxidation[J]. Journal of Adhesion Science and Technology, 2006, 20(4):319-334
- [7]刘艳春,白刚,钱红飞.聚酰亚胺织物的羧基化表面改性[J].纺织学报, 2018(3):103-107.
- [8]高明,黄浩,黄逸凡,等.常压氯气等离子体对碳纤维表面亲水性改性研究[J].集成术, 2018, 7(4):16-23.
- [9]严燕钫,沈艳琴,武海良,等.玄武岩长丝表面低温等离子体处理及其浆丝集束性能[J].纺织学报, 2018, 39(12):24-29.
- [10]郭昌盛,杨建忠,姚一军.连续玄武岩纤维改性方法的研究[J].高科技纤维与应用, 2015, 40(1):24-28.