锦纶6红相特黑色丝的试制
Trial Production of Black Polyamide 6 Fiber

封其都;谭延坤;刘朝新;左传胜;王翠玲;骆晓军;
FENG Qi-du;TAN Yan-kun;LIU Chao-xin;ZUO Chuan-sheng;WANG Cui-ling;LUO Xiao-jun;Yiwu Huading Nylon Co.Ltd.;

摘要(Abstract):

从色母粒性能、纺丝工艺等对锦纶6红相特黑色丝的试制过程进行了研究。试验表明:生产时确保色母粒颗粒均匀,色泽一致,含水率<8×10-4;选择过滤砂和过滤网相结合的过滤方式,组件起始压力14.2 MPa,纺丝温度265℃,丝束上油率0.6%,生产的锦纶黑色丝的灰卡级别为5级,M率为99%。
From the performance of masterbatch and spinning process, the production of black polyamide 6 fibers was studied. Experimental results showed that when using the masterbatch with uniform particles and color consistency, moisture content< 8×104; selecting the filter sand and filter net combination filtration method, the component initial pressure was 14.2 MPa; selecting spinning temperature of 265 ℃, oiling rate of 0.6%, the gray card grade of the black polyamide 6 fiber was 5, the M rate was 99%.

关键词(KeyWords): 锦纶6黑色丝;色母粒;工艺
black polyamide 6 fiber;masterbatch;process

Abstract:

Keywords:

基金项目(Foundation): 国家重点研发计划(2016YFB0302700)

作者(Author): 封其都;谭延坤;刘朝新;左传胜;王翠玲;骆晓军;
FENG Qi-du;TAN Yan-kun;LIU Chao-xin;ZUO Chuan-sheng;WANG Cui-ling;LUO Xiao-jun;Yiwu Huading Nylon Co.Ltd.;

Email:

扩展功能
本文信息
服务与反馈
本文关键词相关文章
本文作者相关文章
中国知网
分享