邵群,文珍稀,林佩洁,郭志洪,倪建华,王依民
SHAO Qun1,WEN Zhen-xi1,LIN Pei-jie1,GUO Zhi-hong1,NI Jian-hua2,WANG Yi-min2 (1.College of Material Science and Engineering

• 1:东华大学材料科学与工程学院
• 2:东华大学纤维材料改性国家重点实验室

摘要(Abstract)：

用Ozawa法和Mo法对聚甲醛(POM)的非等温结晶动力学进行研究。采用双螺杆纺丝机熔融纺得POM初生纤维,再用水浴拉伸方法制得POM纤维,研究拉伸倍数、水浴温度对POM纤维结晶性能的影响。结果表明:在不同的降温速率下,随着降温速率的提高,POM结晶峰峰值温度降低,半结晶时间缩短,结晶速率加快;采用Mo法研究POM的非等温结晶过程比较理想,而Ozawa法不适用;水浴拉伸有利于纤维的结晶,而随着水浴温度的提高,POM纤维的结晶度提高。
Polyoxymethylene(POM) fiber is prepared by two step processes,melt spinning by twin-screw extruder and drawing in a water bath.Experiments are carried out to study the impact of drafting multiple and the temperature of water bath on the crystallization properties of POM fiber￡? and the non-isothermal crystallization kinetics of POM fibers is studied with Mo and Ozawa method.The experimental results show that as the cooling rate is increased,the crystallization peak temperature and half crystallization time decrease,meanwhile the crystallization rate increases at different cooling rate.The Avrami analysis modified by the Mo method can describe the non-isothermal crystallization processes of POM very well,and with the increases of crystallinity,crystallization rate slows down.Drawing is good for the crystallization of fiber and refines the crystalline grain.As the temperature of water bath increases,the crystallization rate increases.

关键词(KeyWords)： 结晶动力学;聚甲醛纤维;拉伸倍数;水浴温度;结晶性能
crystallization kinetic,polyoxymethylene fiber,drafting multiple,the temperature of water bath,crystallization properties

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 邵群,文珍稀,林佩洁,郭志洪,倪建华,王依民
SHAO Qun1,WEN Zhen-xi1,LIN Pei-jie1,GUO Zhi-hong1,NI Jian-hua2,WANG Yi-min2 (1.College of Material Science and Engineering

DOI: 10.16090/j.cnki.hcxw.2011.07.022

参考文献(References)：

• [1]曹玲玲,王勇,王依民.聚甲醛纤维的发展与应用[J].合成技术及应用,2008,23(1):38-41.
• [2]李相明,覃俊,何勇,等.高性能聚甲醛纤维的研究进展与应用[J].合成纤维,2008,37(12):5-9.
• [3]王焕莲,兰建武,刘波,等.聚甲醛的熔融纺丝温度[J].合成纤维,2009,38(4):34-37.
• [4]任敏巧,莫志深.高聚物结晶后期动力学过程的研究进展[J].高分子通报,2003(3):15-22.
• [5]M Avrami.Kinetics of phase changeⅠ:General theory[J].Journal ofChemical Physics,1939,7(12):1 103-1 112.
• [6]M Avrami.Kinetics of phase changeⅡ:Transformation-time relation-ship for random Distribution of Nuclei[J].Journal of Chemical Physics,1939,8(2):212-224.
• [7]Ozawa T.Kinetics of non-isothermal crystallization[J].Polymer,1971(12):150.
• [8]张青兰,郝玉英.POM与POM/TPU共混物非等温结晶动力学的研究[J].中国塑料,2008,22(11):33-37.
• [9]胡友亮.聚甲醛甲醛吸收剂高分子化研究[D].成都:四川大学,2005.