姜正雄,余阳,周美华
JIANG Zheng-xiong,YU Yang,ZHOU Mei-hua(Environmental Science and Engineering Collage

• 1:东华大学环境科学与工程学院

摘要(Abstract)：

采用静电纺丝法制备了不同黏均分子质量(Mη)的聚丙烯腈(PAN)超细纤维毡,并通过280℃预氧化和900℃碳化进一步制备超细碳纤维毡。讨论了Mη对纤维制备的影响,发现PAN的Mη大于3×105则不利于静电纺丝,小于5×104则纤维毡发脆,无法进一步加工处理成碳纤维毡。用场发射扫描电镜、红外光谱、X-射线衍射对纤维毡进行表征,结果表明:随着PAN相对分子质量的升高,碳纤维的直径和得率增大。此外,抗拉强度测试表明:随着相对分子质量的增大,超细碳纤维毡的抗拉强度增加。
PAN superfine carbon fiber mats with different viscosity-average molecular weight(Mη) were fabricated by means of electrospinning,and then preoxidized at 280 ℃ and carbonized at 900 ℃.The effects of PAN molecular weight on the preparation of fiber mats were discussed in detail.It was found that fiber mats could not be obtained through electrospinning if Mη was more than 3×105,and superfine carbon fiber mats could be britvleness when Mη was less than 5×104.The fiber mats were further characterized with field emission scanning electron microscope(FESEM),IR spectrum and XRD pattern.The results exhibited that fiber diameter and the yield rate of carbon fibers were increased with Mη rising.The analysis of fiber's tensile strength showed that the fiber mats' tensile strength was increased with Mη rising.

关键词(KeyWords)： PAN;超细碳纤维毡;预氧化;碳化;抗拉强度
PAN,superfine carbon fiber mat,pre-oxidation,carbonization,tensile strength

Abstract:

Keywords:

基金项目(Foundation): 上海市重点学科建设项目(B604);; 教育部科学技术研究重点项目(107046);; 上海市科学技术委员会重大项目(07DJ14002)

作者(Author): 姜正雄,余阳,周美华
JIANG Zheng-xiong,YU Yang,ZHOU Mei-hua(Environmental Science and Engineering Collage

DOI: 10.16090/j.cnki.hcxw.2010.01.005

参考文献(References)：

• [1]Dai Guiping,Liu Min,et al.Research progress of electrochemical hy-drogen storage in carbon nanotubes[J].New Carbon Materials,2002,17(3):70-74.
• [2]Burcu Ekioglu,Arunan Nadarajah.Structural analysis of conical car-bon nanofibers[J].Carbon,2006,(2):360-373.
• [3]Sarah E Baker,Kiu-Yuen Tse,et al.Fabrication and characterization of vertically aligned carbon nanofiber electodes for biosensing applica-tions[J].Diamond and Related Materials,2006,(2/3):433-439.
• [4]Formhals A.Process and apparatus for artificial threads:US,US1975504[P].1934.
• [5]Simons H.Process and apparatus for producing patterned nonwoven fabrics:US,US3280229[P].1966.
• [6]张旺玺,王艳芝,刘建军等.碳纤维前驱体聚丙烯腈原丝[J].合成纤维,1998,28(1):11-15.
• [7]Young-Wan Jun,Gyoung-Rin Choi,Hong-Ryun Jung.Electrochemi-cal properties of electrospun PAN/MWCNT carbon nanofibers electrodes coated with polypyrrole[J].Electrochimica Acta,2008,53:5796-5803.
• [8]Wang Y,Serrano S,Santiago-Aviles J.Raman characterization of carbon nanofibers prepared using electrospinning[J].Synth Met,2003,138:423-427.
• [9]Ko F,Gogotsi Y,Ali A.Electrospinning of continuous carbon nan-otube-filled nanofiber yards[J].Adv Mater,2003,15(14):1161-1165.
• [10]张旺玺.静电纺丝制备聚丙烯腈纳米碳纤维[J],合成纤维工业,2007,30(5):60-62.
• [11]张旺玺.聚丙烯腈基碳纤维[M].上海:东华大学出版社,2005:38-34.
• [12]复旦大学高分子材料系.高分子实验技术[M].上海:复旦大学出版社,1996:371.