葛鹏飞,葛明桥,魏取福,高卫东
GE Peng-fei, GE Ming-qiao, WEI Qu-fu, GAO Wei-dong (Key Laboratory of Science & Technology of Eco-textiles

• 1:江南大学生态纺织教育部重点实验室
• 2:江南大学生态纺织教育部重点实验室
• 3:江南大学生态纺织教育部重点实验室
• 4:江南大学生态纺织教育部重点实验室 江苏无锡214122

摘要(Abstract)：

采用二氯甲烷为溶剂,以滚筒为收集装置,利用静电纺丝法制备了聚乳酸纳米纤维。分析了溶液体系和滚筒转速对纤维形态结构的影响。结果表明:在质量分数相同的条件下,采用相对分子质量较大的聚乳酸切片所纺纤维直径细而均匀;质量分数增加时,电纺丝产品由一些高分子微/纳米液滴渐变为成形较好、珠状较少的平滑纤维,其平均纤维直径先增加后减小;控制收集滚筒的转速在一定范围内,可以获得排列取向较好的纤维。
Poly(L-lactic acid) nanofibers were prepared via electrospinning by using dichloromethane as a solvent and the rotating cylinder as a collector. The effects of the solution system and the rotating speed of cylinder on the fiber morphology were analysed. The results showed that some thin and uniform fibers were produced using PLLA chips of the high molecular weight under the condition of the same solution concentration. With the increase of the solution concentration, the product of the electrospinning was transformed from some micro/nano macromolecule droplets to some smooth fibers having better forms and less beads. Meanwhile, the average fiber diameter increased firstly then decreased. Some aligned fibers could be obtained by controlling the rotating speed of cylinder in a proper range.

关键词(KeyWords)： 静电纺丝;聚乳酸;溶液体系;滚筒转速;形态结构
electrospinning, poly(L-lactic acid), solution system, the rotating speed of cylinder, morphology

Abstract:

Keywords:

基金项目(Foundation): 教育部先进纺织材料与制备技术重点实验室开放基金资助项目,项目编号2005002。

作者(Author): 葛鹏飞,葛明桥,魏取福,高卫东
GE Peng-fei, GE Ming-qiao, WEI Qu-fu, GAO Wei-dong (Key Laboratory of Science & Technology of Eco-textiles

参考文献(References)：

• [1]Doshi J,Reneker D H.Electrospinning process and applications of electrospun fibers[J].Journal of Electrostatics,1995,35:151-160.
• [2]章金兵,许明.纳米纤维的研究进展[J].江西化工,2004,(3):24-30.
• [3]Yoshimoto H,Shin Y M,et al.A biodegradable nanofiber scaffold by electrospinning and its potential for bone tissue engineering[J].Biomaterials,2003,24:2077-2082.
• [4]胡平,张璐等.电纺丝及其在生物医用材料中的应用[J].纺织科学研究,2004,(2):26-32.
• [5]Koski A,Yim K,et al.Effect of molecular weight on fibrous PVA produced by electrospinning[J].Materials Letters,2004,58:493-497.
• [6]杨清彪,王策等.聚丙烯腈纳米纤维的再细化[J].高等学校化学学报,2004,25(3):589-591.
• [7]Srinivasan G,Reneker D H.Structure and morphology of small diameter electrospun aramid fibers[J].Polymer International,1995,36(2):195-201.
• [8]Deitzel J M,Kleinmeyer J,et al.The effect of processing variables on the morphology of electrospun nanofibers and textiles[J].Polymer,2001,42:261-272.
• [9]Shin Y M,Hohman M M,et al.Experimental characterization of electrospinning:the electrically forced jet and instabilities[J].Polymer,2001,42:9955-9967.