聚乙烯醇-玄武岩混掺纤维水泥砂浆性能研究Study on Properties of Polyvinyl Alcohol and Basalt Mixed Fiber Cement Mortar
许立
XU Li
摘要(Abstract)：
为获得应用性能更好的水泥基复合材料，以聚乙烯醇纤维与玄武岩纤维为混掺对象，保持纤维总体积掺量不变，通过设计不掺纤维、单掺聚乙烯醇纤维、单掺玄武岩纤维以及不同纤维比例混掺等对比方案，对水泥砂浆的流动性、抗压、抗折强度以及干缩性能等进行了研究。结果表明：适当比例的聚乙烯醇纤维和玄武岩纤维混掺，能有效提升水泥砂浆的综合性能；聚乙烯醇纤维和玄武岩纤维体积比为2∶3时，砂浆的韧性、抗裂性均最佳，为最优配比。
In order to obtain cement-based composite materials with better application performance, polyvinyl alcohol fiber and basalt fiber were mixed as the mixing object, and the total volume of fiber was kept unchanged. Through the design of comparative schemes such as no fiber, single polyvinyl alcohol fiber, single basalt fiber and different fiber ratios, the fluidity, compressive, flexural strength and dry shrinkage performance of cement mortar were tested. The results show that the proper proportion of polyvinyl alcohol fiber and basalt fiber can effectively improve the comprehensive performance of cement mortar, the toughness and crack resistance of mortar are the best when the volume ratio of polyvinyl alcohol fiber and basalt fiber is 2∶3.
关键词(KeyWords)：
聚乙烯醇纤维;玄武岩纤维;水泥砂浆;纤维混掺;性能
polyvinyl alcohol fiber;basalt fiber;cement mortar;fiber mixing;property
基金项目(Foundation):
作者(Author):
许立
XU Li
DOI: 10.16090/j.cnki.hcxw.2022.11.002
参考文献(References)：
- [1]王成启,吴科如.混杂纤维水泥基复合材料及其应用[J].工业建筑,2002(9):51-53.
- [2] YANG K H. Tests on concrete reinforced with hybrid or monolithic steel and polyvinyl alcohol fibers[J]. ACI Materials Journal, 2011,108(6):664-672.
- [3]海然,刘俊霞,张茂亮,等.钢-聚乙烯醇混杂纤维超高性能混凝土性能研究[J].混凝土, 2016(5):95-97, 101.
- [4]邓宗才,薛会青.玄武岩纤维混凝土的抗弯冲击性能[J].建筑科学与工程学报, 2009, 26(1):80-83.
- [5]成涛华,李玉香.玄武岩纤维增强混凝土力学性能研究[J].混凝土与水泥制品, 2017(1):53-56.
- [6]刘华挺,张俊芝,傅招旗,等.短切玄武岩纤维混凝土构件抗氯盐侵蚀试验[J].混凝土, 2011(1):14-15.
- [7] ZHAO Y R, WANG L, LEI Z K, et al. Study on bending damage and failure of basalt fiber reinforced concrete under freeze-thaw cycles[J].Construction and Building Materials, 2018, 163:460-470.
- [8] CHAO H J. MCCARTHY T J, CHEN D. et al. Influence of basalt fiber on performance of cement mortar[J]. Key Engineering Materials, 2010, 873(426-427):93-96.
- [9]胡星宇.聚乙烯醇、玄武岩混杂纤维混凝土性能研究[D].合肥:合肥工业大学, 2015.
- [10]于海洋,李地红,代函函,等.混杂纤维增强应变硬化水泥基复合材料的弯曲性能研究[J].材料导报, 2020, 34(S1):229-233.
- [11]何波玲.聚丙烯腈纤维聚合物水泥砂浆性能的研究[D].哈尔滨:哈尔滨工业大学, 2010.
- [12]王英姿,赵帅,田颖,等.聚丙烯纤维增强聚合物水泥砂浆的干缩性能研究[J].硅酸盐通报, 2008(2):403-406.