梁晶晶,张慧茹,孙晋良,任慕苏,邹新国,唐志勇
LIANG Jing-jing,ZHANG Hui-ru,SUN Jin-liang,REN Mu-su,ZOU Xin-guo,TANG Zhi-yong(Research Center of Composite Materials

• 1:上海大学材料科学与工程学院复合材料研究中心

摘要(Abstract)：

合成了一种二酰亚胺化合物(N,N-二乙基间甲基苯甲酰胺),用于制备芳香族聚酰胺织物的抗紫外老化整理剂。通过改变操作条件(浓度、温度、时间),优化整理工艺,并对处理后芳纶织物的性能进行了表征。结果表明:经该整理剂处理过的芳纶织物在320～330 nm有较强的吸收峰;该织物经30 W紫外老化100 h后,强度保持率高达87%,比未经抗老化整理的对照织物样品的抗老化效能提高了一倍,表现出优异的抗紫外老化性能。
In this paper,one kind of diimide compound(N,N-diethyl-m-toluamide) was synthesized,and it was used as protection against UV aging finishing agent for aramid fabrics.The finishing process was optimized and the properties of treated aramid fabrics were characterized.The results showed that the treated aramid fabrics had a strong absorption between 320～330 nm.The tensile strength retention of the treated aramid fabrics after UV-aging 100 h was 87 %,which was doubled compared to untreated blank fabrics.It is found that aramid fabrics after anti-ultraviolet treatment showed excellent ultraviolet resistant properties.

关键词(KeyWords)： 芳香族聚酰胺织物;抗紫外;老化;整理
aramid fabric,anti-ultraviolet,aging,finishing

Abstract:

Keywords:

基金项目(Foundation): 国防科工委项目资助(项目编号MKPT-05-073);; 上海市重点学科建设项目资助(项目编号s30107)

作者(Author): 梁晶晶,张慧茹,孙晋良,任慕苏,邹新国,唐志勇
LIANG Jing-jing,ZHANG Hui-ru,SUN Jin-liang,REN Mu-su,ZOU Xin-guo,TANG Zhi-yong(Research Center of Composite Materials

DOI: 10.16090/j.cnki.hcxw.2011.03.013

参考文献(References)：

• [1]孙晋良,吕伟元.纤维新材料[M].上海:上海大学出版社,2007:75-80.
• [2]郁铭芳.高性能纤维的发展现状和趋势[J].纺织导报,1998,5:2-4.
• [3]黄兴山.芳纶的性能、应用和生产[J].化工时刊,2002,12:1-5.
• [4]刘晓艳,于伟东.几种高性能芳纶纤维的耐光性评价[J].东华大学学报,2007,33(1):96-100.
• [5]J R Brown,N M Browne,P J Burchill,G T Egglestone.Photochemi-cal ageing of Kevlar R 49[J].Textile Research Journal,1983,53:4 214-4219.
• [6]Ghosh L,Fadhilah M H,Kinoshita H,Ohmae N.Synergistic effect ofhyperthermal atomic oxygen beam and vacuum ultraviolet radiationexposures on the mechanical degradation of high-modulus aramid fibers[J].Polymer,2006,47(19):6 836-6 842.
• [7]班燕.TiO2纳米溶胶的制备及其在缓解芳纶纤维紫外光老化中的应用研究[D].上海:东华大学,2005.
• [8]管小红.芳砜纶织物的纳米抗紫外整理[D].上海:东华大学,2009.
• [9]邢哲等.耐紫外线芳1313的制备及力学性能研究[J].陕西科技大学学报,2007,25(5):67-70.
• [10]Ali Khalafi-Nezhad et al.Efficient method for the direct preparationof amides from carboxylic acids using tosyl chloride under solvent-freeconditions[J].Tetrahedron Letters,2005,46(40):6 879-6 882.