曹可,唐国翌,缪春燕,褚晓东
CAO Ke, TANG Guo-yi, MIAO Chun-yan, ZHU Xiao-dong(Graduate School at Shenzhen

• 1:清华大学深圳研究生院新材料所
• 2:清华大学深圳研究生院新材料所
• 3:清华大学深圳研究生院新材料所
• 4:清华大学深圳研究生院新材料所 广东深圳518055

摘要(Abstract)：

以可再生的α-纤维素为基体,粉末发光颗粒作为添加物,利用Lyocell纤维技术制备出发光性能合格的蓄光型自发光纤维。发光Lyocell纤维继承了稀土铝酸盐粉末优异的发光性能,含10%发光材料的纤维其余辉达到了德国的执行标准(DIN67510),10min余辉亮度>20mcd/m2,60 min余辉亮度>2.8 mcd/m2,而其有效余辉(>0.3 mcd/m2)时间大于10h。与无添加的Lyocell纤维相比,其断裂强度下降了17.6%,断裂伸长率上升了25%。
The present study concerned cellulose spinning solutions prepared using N- methylmorpholine-N-oxide (NMMO) as solvent. These solutions were modified with the lanthanide aluminates long afterglow luminescent material. Such spinning solutions allowed to obtain long afterglow luminescent fibers of the Lyocell type. The luminescent Lyocell fibers inherited the excellent long afterglow capability of lanthanide aluminates. The fibers containing 10 % lanthanide aluminates could achieve Germanic standard, afterglow brightness >20 mcd/m2 in 10 min, >2.8 mcd/m2 in 60 min. Furthermore, the effective afterglow time of the fiber was more than 10 hours. Compared with the non-additional Lyocell fibers, the tensile strength of these luminescent Lyocell fibers decreased by 17.6 %, but the fracture elongation ratio increasd by 25 %.

关键词(KeyWords)： Lyocell纤维;发光纤维;稀土铝酸盐;余辉亮度
Lyocell fiber, luminescent fiber, lanthanide aluminates, long afterglow luminescent material

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 曹可,唐国翌,缪春燕,褚晓东
CAO Ke, TANG Guo-yi, MIAO Chun-yan, ZHU Xiao-dong(Graduate School at Shenzhen

参考文献(References)：

• [1]Piotr C.Thermal and rheological characterization of cellulose spinning dopes modified with nanosilica and antibacterial agents[J].Polymers for Advanced Technologies,2007,18:845-852.
• [2]徐长富,张锦虹,刘欣等.蓄光型发光丙纶[J].合成纤维,2003,32(5):20-21.
• [3]黄碧玉.蓄光纤维的开发与工艺讨论[J].合成纤维,2006,35(8):32-33.
• [4]肖志国.蓄光型发光材料及其制品[M].北京:化学工业出版社,2002:149.
• [5]储德清,王立敏,尹航,高尚.纳米稀土发光纤维的研究与展望[C]//第六届功能性纺织品及纳米技术研讨会论文集.北京:北京纺织工业学会,2006:145-147.
• [6]金立国,汪晓峰,刘强.Lyocell纤维纺丝工艺[J].合成纤维,1998,27(1):18-22.