范春民;王亚松;
FAN Chun-min;WANG Ya-song;Jiangsu Hengke New Material Co., Ltd.;

• 1:江苏恒科新材料有限公司

摘要(Abstract)：

介绍了一种超亮光内三角中空仿锦纶涤纶全拉伸丝(FDY)生产工艺，通过对喷丝板的设计、纺丝和卷绕工艺等进行试验，探索得到最佳工艺参数。试验表明，在纺丝温度291～295℃、冷却风温度22℃、风速1.55 m/s、GR_1速度4 750 m/s、GR_2速度4 800 m/s、GR_2温度120℃、卷绕速度4 800 m/s的工艺条件下，生产的FDY的断裂强度为2.77 cN/dtex，断裂伸长率为45.1%，中空度为15%。
The production process of super-bright inner triangle hollow imitated polyamide polyester full drawn yarn(FDY) was introduced.The optimum process parameters were obtained by experiments on the design of spinneret,spinning and winding process,etc.The test shows that under the spinning temperature of291～295℃,cooling air temperature of 22℃,wind speed of 1.55 m/s,GR_1speed of 4 750 m/s,GR_2speed of 4 800 m/s,GR_2temperature of 120℃,winding speed of 4 800 m/s,the breaking strength of the produced FDY is 2.77 cN/dtex,elongation at break is 45.1%,and hollow degree is 15%.

关键词(KeyWords)： FDY;仿锦纶;异形喷丝板;纺丝工艺;卷绕工艺
FDY;imitated polyamide fiber;shaped spinneret;spinning process;winding process

Abstract:

Keywords:

基金项目(Foundation):

作者(Authors): 范春民;王亚松;
FAN Chun-min;WANG Ya-song;Jiangsu Hengke New Material Co., Ltd.;

DOI: 10.16090/j.cnki.hcxw.2023.01.010

参考文献(References)：

• [1]刘让同,李锐.喷丝板的设计生产[J].轻纺工业与技术, 2011, 40(1):17-20.
• [2]杨元坤.高速纺涤纶中空长丝的研制[J].合成纤维工业, 2002, 25(5):47-50.
• [3]张建国,岳花林,李海涛,等. 55 dtex/36 f中空涤纶全拉伸丝的开发[J].合成纤维工业, 2010, 33(3):53-55.
• [4]王华平,余晓蔚,朱建民.熔纺中空纤维皮芯结构的形成原理及动力学模拟[J].合成纤维工业, 1999, 22(5):1-4.