董葳,陈晟辉,汪晓峰,张玉梅,王华平
DONG Wei,CHEN Sheng-hui,WANG Xiao-feng,ZHANG Yu-mei,WANG Hua-ping

• 1:东华大学材料学院
• 2:纤维材料改性国家重点实验室
• 3:上海特安纶纤维有限公司

摘要(Abstract)：

利用旋转流变仪研究了聚芳砜酰胺(PSA)纺丝液的稳态和动态流变行为,结果表明:以二甲基乙酰胺(DMAc)为溶剂的聚芳砜酰胺溶液表现出典型的聚合物浓溶液流变特性,在低剪切速率区表现为牛顿流体特性,而随着剪切速率的增大,呈现出切力变稀行为,纺丝液的零切黏度、松弛时间随PSA特性黏度的增大而增大,非牛顿特性增强;证明了PSA纺丝溶液在测试温度范围内处于均质溶液状态,在进一步的动态温度扫描分析中,没有发现溶液的凝胶化转变现象,说明在试验温度范围内,PSA纺丝液处于均质稳定状态。
The rheological behavior of polysulfonamide(PSA) spinning dope was studied using rotational rheometer. A typical behavior of concentrated polymer solution was observed. The non-Newtonian behavior was shown from the increase of zero viscosity and relaxation time of the spinning dope with increasing the intrinsic viscosity of PSA. The dynamic rheological behavior of PSA spinning dope, proved the spinning dope had the characteristic of homogeneous solution in the range of experimental temperature. No gelation transition was observed from the further temperature sweep analysis, which also indicated that the spinning dope of PSA was uniform and stable.

关键词(KeyWords)： 聚芳砜酰胺;纺丝溶液;流变特性;稳定性
polysulfonamide;spinning dope;rheological behavior;stability

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金(51273039)资助

作者(Author): 董葳,陈晟辉,汪晓峰,张玉梅,王华平
DONG Wei,CHEN Sheng-hui,WANG Xiao-feng,ZHANG Yu-mei,WANG Hua-ping

DOI: 10.16090/j.cnki.hcxw.2013.11.012

参考文献(References)：

• [1]余优霞,陈晟辉,袁峥,等.氯化钙对间位聚芳砜酰胺/二甲基甲酰胺溶液的影响[J].合成纤维,2013,42(1):7-12.
• [2]Yang H H.Aromatic high-strength fibers[M].New York:Wiley,1989:66-289.
• [3]Hsiao S H,Chang Y H.New soluble aromatic polyamides containing ether linkages and laterally attached p-terphenyls[J].European Polymer Journal,2004,40(8):1 749-1 757.
• [4]Olabisi O.Handbook of Thermoplastics[M].New York:Marcel Dekker,1997.
• [5]汪晓峰,张玉华.芳砜纶的性能及其应用[J].纺织导报,2005(1):18-20.
• [6]汪晓峰.芳香族聚砜酰胺纤维的制造方法:CN,1389604A[P].2003-01-08.
• [7]沙玉明.芳香族聚砜酰胺纤维的制造方法:CN,101255616A[P].2007-03-02.
• [8]Dibrova A,Schetinin A,Kudryavtsev G.Properties of solutions of poly-4,4′-diphenylsulfone terephthalamide[J].Fibre Chemistry,1979,10(4):323-332.
• [9]Chen Y,Wu D,Li J,et al.Physicochemical characterization of two polysulfonamides in dilute solution[J].Macromolecular Symposia,2010,298(1):116-123.
• [10]Wu D,Chen X,Chen S,et al.Rheological Characterization of Poly(3,3′-Diaminodiphenylsulfone Terephthaloylchloride)Solutions in Dimethylsulfoxide[J].Journal of Macromolecular Science,Part B,2012,52(3):504-511.
• [11]Gashinskaya N A,Prozorova G E,Vasil'eva N V,et al.Gelation of polysulfonamide solutions[J].Fibre Chemistry,1976,8(3):300-303.
• [12]Vasil'eva N,Prozorova G,Shchetinin A.Nature of the solvent and the temperature as factors in the viscosity properties of polysulfonamide solutions[J].Fibre Chemistry,1976,8(2):195-198.
• [13]Dibrova A,Glazunov V,Papkov S.Interaction in the system polymer-dipolar aprotic solvent-salt[J].Fibre Chemistry,1987,18(3):180-183.
• [14]倪如青,陈蕾,刘兆峰,等.芳砜纶纺丝溶液的流变性能研究[J].合成纤维,2005,34(6):6-9.
• [15]陈蕾,胡祖明,刘兆峰.芳纶1313纺丝原液的流变性能研究[J].合成纤维,2004,33(6):7-9.
• [16]Colby R H,Boris D C,Krause W E,Dou S.Shear thinning of unentangled flexible polymer liquids[J].Rheologica Acta,2007,46(5):569-575.
• [17]Byron Bird R,Carreau P J.A nonlinear viscoelastic model for polymer solutions and melts[J].Chemical Engineering Science,1968,23(5):427-434.
• [18]Devasia R,Nair C P R,Ninan K N.Temperature and shear dependencies of rheology of poly(acrylonitrile-co-itaconic acid)dope in DMF[J].Polymers for Advanced Technologies,2008,19(12):1 771-1 778.
• [19]Chen X,Zhang Y M,Cheng L Y,et al.Rheology of concentrated cellulose solutions in 1-Butyl-3-methylimidazolium Chloride[J].Journal of Polymer Environment,2009,17(4):273-279.
• [20]Rubinstein M,Colby R.Polymer Physics[M].New York:Oxford University Press,2003.
• [21]Han C D,Kim J W,Kim J K.Determination of the order-disorder transition temperature of block copolymers[J].Macromolecules,1989,22(1):383-394.
• [22]Winter H H,Chambon F.Analysis of linear viscoelasticity of a crosslinking polymer at the gel point[J].J Rheol.1986,30(2):367-382.
• [23]Winter H H,Mours M.Rheology of polymers near liquid-solid transitions in neutron spin echo spectroscopy viscoelasticity rheology[M].Berlin:Springer-Verlag,1997:134,165-234.
• [24]Chambon F,Winter H H.Linear viscoelasticity at the gel point of a crosslinking PDMS with imbalanced stoichiometry[J].Journal of Rheology,1987,31(8):683-697.
• [25]Nijenhuis K T,Winter H H.Mechanical properties at the gel point of a crystallizing poly(vinyl chloride)solution[J].Macromolecules,1989,22(1):411-414.