张军,李文刚,陈大中,罗卫
ZHANG Jun,LI Wen-gang,CHEN Da-zhong,LUO Wei(Donghua University

• 1:东华大学材料学院纤维材料改性国家重点实验室

摘要(Abstract)：

利用差示扫描量热法(DSC)、X-射线衍射(XRD)和声速取向等测试手段,研究了聚萘二甲酸乙二酯(PEN)纤维加工成为帘子线过程中要经受的高温热处理过程中的内部结构变化,并利用万能材料测试仪研究了纤维的力学性能。试验结果表明:PEN纤维在加工过程中结晶度增大;PEN纤维的α型晶粒尺寸变大,结晶结构趋于完善;纤维在热处理中取向度没有明显的变化;经过热处理后纤维力学强度提高,而断裂伸长率下降。
Polyethylene naphthalate(PEN) fiber was treated with high temperature in the course of cord fabrication.The changes of internal structure in the high-temperature treatment were studied by differential scanning calorimeter(DSC),X-ray diffraction(XRD),sonic orientation and other testing methods.The mechanical properties were investigated using universal material tester in this paper.The results showed that the degree of crystallinity of PEN fiber was increased,the α crystal form of PEN fiber became bigger and the crystalline structure was better.The degree of orientation was mensurated by sonic orientation law and it was not changed significantly.The mechanical strength increased and specific elongatioat break decreased.

关键词(KeyWords)： 聚萘二甲酸乙二酯;热处理;结晶;结晶尺寸;力学性能
polyethylene naphthalate,heat treatment,crystalline,crystallite size,mechanical property

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 张军,李文刚,陈大中,罗卫
ZHANG Jun,LI Wen-gang,CHEN Da-zhong,LUO Wei(Donghua University

DOI: 10.16090/j.cnki.hcxw.2011.01.009

参考文献(References)：

• [1]贾广霞,安树林等.热处理过程对锦纶6帘子线性能的影响[J].天津工业大学学报,2004,23(2:)14-16.
• [2]魏孟媛,杨革生等.热处理对轮胎帘子线用Lyocell纤维性能的影响[J].合成纤维工业,2008,31(8:)18-21.
• [3]喻爱芳.ET/CT共聚酯的制备及结构性能研究[D]:上海:东华大学,2005.
• [4]S Z D Cheng and B Wunderlich.Glass transition and melting behaviorof poly(ethylene-2,6-naphthalenedicarboxylate)[J].Macromolecules,1988,21(3):789-797.
• [5]Buchner,S,Wiswe,D,Zachmann,H G.Kinetics of crystallization andmelting behaviour of poly(ethylene naphthalene-2,6-dicarboxylate)[J].Polymer,1989,30(3):480-488.
• [6]Nagai A,Murase Y,et al.Fiber properties of poly(ethylene 2 6-naphthalenedicarboxylate)obtained by high speed spinning[J].纖維学会誌,1995,51(10):470-477.
• [7]Nagai A,Murase Y,et al.Structural change of crystal modifications ofpoly(ethylene 2 6-naphthalenedicarboxylate)fiber obtained by high speedspinning[J].纖維学会誌,1995,51(10):478-483.
• [8]尹宝.高模低缩涤纶工业丝结构、性能特点的研究[D]:上海:东华大学,2007.