熔纺氨纶废丝的回收再利用Study on the Recycle and Reuse of Melt-spun Polyurethane Fiber Waste
钱健斌,王静荣,陈大俊
QIAN Jian-bin; WANG Jing-rong; CHEN Da-jun (State Key Lab.for Modifcaition of Chemical Fibers and Polymer Materials;
摘要(Abstract)：
采用升温红外光谱分析法,探讨了熔纺氨纶废丝在升温过程中分子链断裂的机理。在此基础上,提出在磷酸三乙酯介质中,以乙酰胺对废丝进行热降解,使其获得重新加工的性能的方法。进一步,将降解产物与新鲜的聚四氢呋喃二醇(PTMG)混合,然后与甲苯二异氰酸酯(TDI)进行反应,制成了再生聚氨酯薄膜。
In this paper melt-spun polyurethane fiber waste has been thermo-degraded in triethylene phos-phonate by adding acetamide. The influences of reaction time and reaction temperature on the degree of degradation have been studied. The results show that the melt-spun polyurethane fiber waste can obtain the re-process ability by this method. The proper thermo- degradation condition is 170 ℃, 30min. The recycled polyurethane film has been synthesized by mixing the degraded product with fresh PTMG and then reacting with TDI. The tensile strength of the recycled polyurethane film is about 2￣4 times higher than that of the degraded product. The initial weight loss of the recycled film is about 220 ℃. With the increasing of de- graded product content, the temperatures of the initial weight loss decrease.
关键词(KeyWords)：
熔纺氨纶废丝;回收;再利用
melt-spun polyurethane fiber waste,recycle,reuse
基金项目(Foundation):
作者(Authors):
钱健斌,王静荣,陈大俊
QIAN Jian-bin; WANG Jing-rong; CHEN Da-jun (State Key Lab.for Modifcaition of Chemical Fibers and Polymer Materials;
参考文献(References)：
- [1]杨涛锋,陈大俊,李瑶君.熔纺氨纶的制备方法及性能.聚氨酯工业,2000,15(1):1.
- [2]Chen Dajun,Li Yaojun.Hydrogen Bonding in Thermoplastic Polyurethane Elastermers:IR Thermal Analysis.Chemical Research in Chinese University,2002,18(1):84.
- [3]Skrovanek,D J,Howe,S E,Painter,P C,and Coleman,M M.Hydrogen bonding in polymers,Macromolecules,1985,18(7):1676.
- [4]李俊贤,叶菁萱,修玉英等.北京:聚氨酯工业手册,1999.11.