朱兰芳,李亚滨
ZHU Lan-fang,LI Ya-bin(School of Textiles

• 1:天津工业大学纺织学部

摘要(Abstract)：

通过热失重(TG)及差示扫描量热分析(DSC),对聚乳酸纤维与涤纶的热学性能进行对比测试,同时还测试了聚乳酸纤维的热收缩率和极限氧指数。结果表明:随着温度升高,聚乳酸纤维的TG-DTG曲线有2个失重台阶,在330℃左右开始热分解,主失重温度约为360℃;聚乳酸纤维的DSC曲线呈现出双熔融峰,较低熔融峰为161.6℃,较高熔融峰为169.9℃;聚乳酸纤维的沸水收缩率和干热空气收缩率分别为12%和4.5%;聚乳酸纤维的极限氧指数为27%。
TG and DSC are used to analyze the thermal property of polylactic acid(PLA) fibers and compared with polyester(PET) fibers.The heat shrinkage and limited oxygen index of the PLA fibers are also tested.The investigation showes that as the temperature increases,the PLA fibers′ TG curves appear two weight loss bands.It begins to decompose at about 330 ℃,and the main weight loss temperature is about 360 ℃.Compared with PET fibers,the PLA fibers′ DSC curve appears double melting peaks.The higher melting peak appears at 169.9 ℃,and the lower one appears at 161.6 ℃.The heat shrinkages of PLA fibers in boiling water and hot air are 12 % and 4.5 % respectively.The limited oxygen index of the PLA fiber is 27 %.

关键词(KeyWords)： 聚乳酸纤维;涤纶;热学性能
PLA fiber,PET fiber,thermal property

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 朱兰芳,李亚滨
ZHU Lan-fang,LI Ya-bin(School of Textiles

DOI: 10.16090/j.cnki.hcxw.2012.11.005

参考文献(References)：

• [1]S Viju G Thilagavathi.Recent developments in PLA fibers[J].Chemical Fibers International,2009,59(3):154-155.
• [2]陈昂,钱明球.聚乳酸的聚合、纺丝、性能及其织物的开发[J].合成纤维,2005,34(9):1-6.
• [3]张红,刘鸿.热分析技术在高分子材料研究中的应用[J].广州化工,2001,29(4):39-42.
• [4]张幼珠.纺织应用化学[M].上海:东华大学出版社.
• [5]许蓓,孙和平.用反相气相色谱法研究聚酯纤维的玻璃化转变温度及探针分子的选择[J].合成纤维,1999,28(6):18-22.
• [6]熊春华,张传杰,张楠楠,等.PLA纤维的性能研究[J].武汉纺织大学学报,2011,24(3):7-10.
• [7]李亚滨,寇士军.阻燃处理对聚乳酸纤维性能的影响[J].纺织学报,2006,27(4):28-30.