周建军,孔海娟,张蕊,马禹,滕翠青,余木火
ZHOU Jian-jun,KONG Hai-juan,ZHANG Rui,MA Yu,TENG Cui-qing,YU Mu-huo (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

• 1:东华大学纤维材料改性国家重点实验室

摘要(Abstract)：

借助超临界二氧化碳的溶胀及携带性能,将六亚甲基二异氰酸酯(HD)I携带进入芳纶中,并对纤维进行改性,利用力学性能测试、红外光谱、扫描电镜、X-射线光电子能谱方法测试了纤维的力学性能以及纤维与基体树脂的界面黏附性能,观察了纤维的表面形貌,分析了纤维表面的元素分布等。结果表明:经改性的纤维强度及模量均有提高;纤维表面变得粗糙,N元素含量明显增加,极性基团增加;复合材料界面剪切强力明显增加,表明纤维更适合用作复合增强材料。
The swelling and carrying ability of supercritical carbon dioxide were used to swell aramid fiber and carry hexamethylene diisocyanate(HDI) into fiber to modify the aramid fiber.Also,the mechanical properties of modified fiber and the adhesive ability with resin weae tested,the surface topography was observed,the surface element distribution was analysed.The results showed that the fiber strength and modulus weae improved,fiber surface became rougher,the content of nitrogen raised obviously,polar group increased,the extraction from resin became harder.All indicated that the fiber was more suitable to act as an enhancement part for resin.

关键词(KeyWords)： 芳纶;超临界二氧化碳;改性;六亚甲基二异氰酸酯
aramid fiber,supercritical carbon dioxide,modification,hexamethylene diisocyanate

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 周建军,孔海娟,张蕊,马禹,滕翠青,余木火
ZHOU Jian-jun,KONG Hai-juan,ZHANG Rui,MA Yu,TENG Cui-qing,YU Mu-huo (State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

DOI: 10.16090/j.cnki.hcxw.2012.05.002

参考文献(References)：

• [1]金辉,王一雍.芳纶纤维表面改性技术及相关机理的研究进展[J].化工新型材料,2009,37(3):24-26.
• [2]刘克杰,杨文良,彭涛,等.芳纶表面改性技术发展(一)———物理改性方法[J].合成纤维,2011,40(6):25-29.
• [3]刘克杰,杨文良,彭涛,等.芳纶表面改性技术发展(二)———化学改性方法[J].合成纤维,2011,40(7):26-31.
• [4]尤志强,胡祖明,陈蕾,等.Technora纤维的表面改性研究[J].高科技纤维与应用,2009,34(1):30-33.
• [5]叶树集,陈鸣才,黄玉惠,等.超临界CO 2溶胀聚合物的研究及其应用[J].广州化学,1999,(1):59-64.
• [6]金俊弘,罗开清,江建明,等.离子基团对PBO纤维的表面性能及其界面粘结性能的影响[J].复合材料学报,2006,23(6):69-74.
• [7]中西香尔,P H索罗曼.红外光谱100例[M].北京:科学出版社,1984:10-11.
• [8]L S Penn,B Jutis.The effect of pendent croups at the fiber surface on interfacial adhesion[J].The Journal of Adhesion,1989,30(1-4):67-81.