郭静,徐德增,冯伟军,石铮
GUO Jing, XU De-zeng, FENG Wei-jun, SHI Zheng (Dalian Polytechnic University

• 1:大连工业大学
• 2:大连工业大学
• 3:大连工业大学
• 4:大连工业大学 辽宁大连116034

摘要(Abstract)：

以氧化锌(ZnO)为抗菌剂、水溶性聚酯(COPET)为成孔剂,通过共混纺丝和碱处理,制备了具有多孔结构的、具有吸湿和抗菌功能的聚丙烯(PP)纤维。研究发现,PP/COPET/ZnO三元共混物的密度和结晶度随COPET含量增加而增大;COPET质量分数为9%的共混物的结晶特性略优于3%的;COPET质量分数为6%时纤维的保水率最大;共混纤维对大肠杆菌、枯草杆菌、八叠球菌均有抗菌敏感性。
With ZnO as antimicrobial agent and COPET as pore-forming agent, moisture absorption and antibacterial polypropylene fiber was obtained by blend spinning and alkali treatment. The fiber had multiporous structure. The results showed that the density and crystallinity of PP/COPET/ZnO blends were increased with the increase of the COPET component. The crystallinity of the blends that the mass fraction of COPET was 9 % was better than the blends that the mass fraction of COPET was 3 %. The water-retention of the blend fiber had maximum value when the mass fraction of COPET was 6 %. The blend fibers were sensitive to Escherichia coli, Bacillus Subtilius and Sarcina, especially to Bacillus Subtilius.

关键词(KeyWords)： PP/COPET/ZnO;共混纤维;结晶性;吸水性;抗菌性
PP/COPET/ZnO, blend fiber, crystallinity, moisture absorption, antibacterial property

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 郭静,徐德增,冯伟军,石铮
GUO Jing, XU De-zeng, FENG Wei-jun, SHI Zheng (Dalian Polytechnic University

参考文献(References)：

• [1]郭静,孟莉莉,徐德增等.PP/WSPET/ZnO三元共混合金的流变性研究[J].合成纤维,2007,36(7):34-37.
• [2]何曼君,陈维孝,董西侠.高分子物理(修订版)[M].上海:复旦大学出版社,2002:9.
• [3]顾利霞,刘兆峰.亲水性纤维[M].北京:中国石化出版社,1997:2.