甘宇,姬洪,徐锦龙,张玉梅
GAN YU,JI Hong,XU Jin-long,ZHANG Yu-mei

• 1:东华大学材料科学与工程学院纤维材料改性国家重点实验室
• 2:浙江恒逸石化有限公司

摘要(Abstract)：

聚酯纤维具有模量高、价格低廉的优点,但是存在静电和不易着色;而聚酰胺纤维具有较好的染色性、吸湿性等优点,但是模量较低且成本较高。为充分利用聚酰胺和聚酯的优点而克服因两者相容性差导致的成形问题,从原料黏弹性、挤出成形温度、热拉伸等多个方面入手,探讨提高聚酰胺/聚酯皮芯复合纺丝稳定性的技术方案。流变和纺丝试验结果表明:缩小熔体温度差,使聚酯和聚酰胺熔体黏度相近时,可制备结构稳定、性能较好的皮芯复合纤维;在拉伸温度偏向聚酯组分的拉伸温度时,聚酰胺/聚酯皮芯复合纤维的皮层和芯层组分更易做到同步拉伸;所制备的复合纤维平衡回潮率>2%,并且可以采用常规酸性染料染色,避免了常规聚酯纤维高温高压染色且因染色过程中碱减量造成的环境污染。
Polyester fiber has the advantages of high modulus and low cost, but has the disadvantage of static electricity and difficult to color. Polyamide fiber has better dyeing and hygroscopicity, but it has lower modulus and higher costs. In order to make full use of the advantages of polyamide and polyester, the viscoelasticity of chips, extrusion temperature and the process hot drawing were discussed to overcome the forming problems caused by poor compatibility. The optimized spinning solutions for the sheath-core spinning were proposed. The results show that the sheath-core composite fiber with stable structure and good performance can be prepared with similar melting temperature difference and viscosity. When the stretching temperature is biased toward the stretching temperature of the polyester component, the skin layer and the core layer component of the polyamide/polyester core-sheath composite fiber are more easily subjected to simultaneous stretching. The prepared composite fiber can be dyed with a conventional acid dye with the equilibrium moisture regain ratio larger than 2%. This avoids the use of high temperature and high pressure to dye conventional polyester fibers and environmental pollution due to alkali reduction during dyeing.

关键词(KeyWords)： 皮芯复合纤维;聚酯;聚酰胺;吸湿;染色
sheath-core composite fiber;polyester;polyamide;moisture absorption;dyeing

Abstract:

Keywords:

基金项目(Foundation): 浙江恒逸石化有限公司技术开发项目资助

作者(Author): 甘宇,姬洪,徐锦龙,张玉梅
GAN YU,JI Hong,XU Jin-long,ZHANG Yu-mei

DOI: 10.16090/j.cnki.hcxw.2020.02.002

参考文献(References)：

• [1]魏家瑞.热塑性聚酯及其应用[M].北京:化学工业出版社,2012:115-120.
• [2]朱建民.聚酰胺纤维[M].北京:化学工业出版社,2014:196-205,235.
• [3]李良训,黄素萍,章潭莉,等.锦涤纶复合丝的工艺研究第一部分:纺丝和拉伸工艺研究[J].华东纺织工学院学报,1981(1):57-62.
• [4]林金锭.涤锦皮芯型复合长丝的性能[J].合成纤维,1981,10(6):17-21.
• [5]孙桐,江浩,黄素萍,等.锦涤纶皮芯型复合纤维拉伸热的静态模拟计算[J].合成纤维,1982,11(4):1-5.
• [6]吴建亭.PET/PA6复合纺丝工艺的确定[J].聚酯工业,2010,23(5):44-46.
• [7]黄洁希,林海,王增喜,等.皮芯型涤锦复合纤维FDY生产工艺探讨[J].化纤与纺织技术,2017,46(2):1-4.
• [8]袁孟红,金惠芬,黄素萍,等.高强高模锦/涤皮芯复合长丝工艺的探索[J].合成纤维,1995,24(1):13-17.
• [9]SOUTHERN J H,MARTIN D H,BAIRD D G.Improved sheath/core adhesion in biconstituent fibers via interface mixing[J].Textile Research Journal,1980,50(7):411-416.
• [10]姜浩然,纪庭璋,朱志祥.锦涤复合皮芯短纤维生产工艺[J].合成纤维工业,2001(2):44-46.