董晓敏,王进美,支超
DONG Xiao-min,WANG Jin-mei,ZHI Chao(School of Textile and Materials

• 1:西安工程大学纺织与材料学院

摘要(Abstract)：

采用聚丙烯酸酯树脂涂层结合纳米拒水拒油剂的复合整理工艺路线,对涤纶织物进行耐酸和耐碱整理。使用占布质量60%的树脂和8%的纳米整理剂分两步处理织物,烘干温度为80℃,烘焙温度为160℃,烘焙时间3 min,按国家标准测试方法测试,经处理的涤纶织物在洗前和洗后,耐酸碱透过时间均可达到3 min及以上。经处理织物手感柔软,透气性良好,能较好保持原有的服用性能,同时具有良好的耐水洗性能。
The polyester fabric was treated with polyacrylate resin and nano water and oil repellent agents for acid and alkali resistance.The fabric was treated by 60 % resin of total fabric weight and 8 % nano finishing agent with conditions of drying temperature 80 ℃,baking temperature 160 ℃,baking time 3 min.After examination with national standard test method,the anti-through time for acid and alkali was achieved both 3 min before and after washing.The fabric was soft and breathable after finishing,which maintained the original wearability and good washing performance.

关键词(KeyWords)： 聚丙烯酸酯;纳米整理剂;耐酸和耐碱;耐水洗
polyacrylate,nano-finishing,acid and alkali resistance,fastness to washing

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 董晓敏,王进美,支超
DONG Xiao-min,WANG Jin-mei,ZHI Chao(School of Textile and Materials

DOI: 10.16090/j.cnki.hcxw.2011.09.012

参考文献(References)：

• [1]吴建华,华载文,王忠霞.耐久性防酸防碱防水透湿涂层布的研究[J].印染,20002,6(11):30-31.
• [2]汪多仁.丙烯酸系乳液涂层整理[J].产业用纺织品,2001,19(8):38-39.
• [3]刘吉平,郝向阳.纳米功能复合材料[M].北京:国际工业出版社,2003.
• [4]GB 24540—2009防护服装酸碱类化学品防护服[S].