李丹曦,马亚运,高晓平
LI Dan-xi,Ma Ya-yun,GAO Xiao-ping

• 1:内蒙古工业大学轻工与纺织学院

摘要(Abstract)：

详细阐述了四轴向经编玻璃纤维织物树脂膜溶渗成型工艺,测试了成型后的复合材料性能,并与同样条件下手糊成型工艺进行对比。结果表明:由于树脂膜溶渗成型工艺复合材料中的纤维体积含量要高于手糊成型工艺,因此其试样的断裂强力、断裂伸长率要高于手糊成型;另外,树脂膜溶渗成型复合材料试样沿不同取向断裂强力由高到低分别是经向、斜向、纬向;经真空辅助成型制备的材料相比手糊成型具有较优异的韧性。
The resin film infusion molding process of four-axial warp knitted composite is described in de-tail.The performance of the composite materials is tested.Compared with hand lay-up molding process atthe same time,the composite fiber volume content in the resin film infusion molding process is superior tohand lay-up molding process.In the tensile test,breaking strength,elongation at break of the resin film infu-sion samples are higher than that of hand lay-up molding.Tensile mechanical properties tests along the dif-ferent orientation from high to low are warp,oblique and weft.Materials prepared by resin film infusion hasexcellent toughness.

关键词(KeyWords)： 复合材料;多轴向经编织物;树脂膜溶渗;拉伸性能;弹性模量
composite;multi-axial warp knit;resin film infusion;tensile property;elastic modulus

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 李丹曦,马亚运,高晓平
LI Dan-xi,Ma Ya-yun,GAO Xiao-ping

DOI: 10.16090/j.cnki.hcxw.2015.12.009

参考文献(References)：

• [1]王善元,张汝光.纤维增强复合材料[M].上海:中国纺织出版社,1998:25-45.
• [2]顾宏梅,徐建如,冯李军.复合材料用经编针织物的研制与应用[J].纤维复合材料,2003(3):21-23.
• [3]罗永康.经编复合材料及其应用[J].航天工艺,1999(4):31-36.
• [4]赵鸿汉,环氧基纤维增强复合材料应用面面观[J].玻璃纤维,2006(1):42-46.
• [5]王芳.VARTM用环氧树脂固化工艺的研究[J].高科技纤维与应用,2006,31(1):41-44.
• [6]王汝敏,蓝立文.先进复合材料用热固性树脂基体的发展[J].热固性树脂,2001,16(1):36-38.
• [7]周华,张万平.玻纤产业织物的发展[J].玻璃纤维,2006(1):33-37.