阳知乾,余晓华,李文刚
YANG Zhi-qian1, YU Xiao-hua2, LI Wen-gang1 (1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

• 1:东华大学纤维材料改性国家重点实验室
• 2:上海华源股份有限公司常州化纤公司
• 3:东华大学纤维材料改性国家重点实验室 上海200051
• 4:江苏常州213016

摘要(Abstract)：

采用差示扫描量热仪,对二苯基硅二醇改性PET的非等温结晶动力学进行了研究,利用Jeziorny动力学模型对结晶过程进行拟合计算。结果表明:改性PET的Avrami指数偏大,其原因是由于二苯基硅二醇的加入,改变了其结晶成核方式;与纯PET相比,半结晶时间增加。用Ziabicki方法处理得出的结晶能力参数Gc值也说明了改性PET的结晶能力比纯PET好。
The nonisothermal crystallization of modified PET by diphenylsilanediol was studied by differential scanning calorimetry. Its crystallization behavior was analyzed with a kinetic model. The results showed that the Avrami exponent was larger than neat PET. It is possible that the mechanism of nucleation and on the form of crystal growth had changed for adding the diphenylsilanediol, the half-time of crystallization was increased. The value of kinetic crystallizability Gc from Ziabicki theory was consistent with the preceding results, it concluded that the crystallizability of modified PET was better than neat PET.

关键词(KeyWords)： 二苯基硅二醇;改性PET;非等温结晶动力学
diphenylsilanediol, modified PET, nonisothermal crystallization kinetics

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 阳知乾,余晓华,李文刚
YANG Zhi-qian1, YU Xiao-hua2, LI Wen-gang1 (1. State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

参考文献(References)：

• [1]Funakoshi wataru.Pilling-resistant polyester fibers[P].JP53124562.1977-04-07.
• [2]Andreas Maurer.Non-pilling polyester fibers[P].US20040143054A1.
• [3]李凤艳.抗起球阻燃聚酯的研究[J].聚酯工业,2002,15(4):20-24.
• [4]张野.抗起球聚酯及其纤维的开发[J].聚酯工业,2006,19(1):24-26.
• [5]Pitt Supaphol.Nonisothermal melt-crystallization kinetics for three liner aromatic polyesters[J].Thermochemica acta,2003,406:211.
• [6]Ziahieki A.Kinetics of polymer crystallization and molecular orienta-tion in the course of melt spinning[J].Appl Polymer Symp,1967,6:1.
• [7]Ozawa T.Kinetics of non-isothermal crystallization[J].Polymer,197l,(12):150.
• [8]Andrzej Jeziorny.Parameters characterizing the kinetics of the non-isothermal crystallization of poly(ethylene terephthalate)determined by DSC[J].Polymer,1978,(19):1142.
• [9]A Duillard.A comparative model for anisothermal and isothermal crystallization of poly(ethylene terephthalate)[J].Polymer,1993,34:1702.
• [10]A Ziabicki.Polymer,1967,12:405.
• [11]张志英.表征高聚物非等温结晶动力学的参数-动力学结晶能力[J].合成纤维工业,1999,13(6):34.
• [12]Pitt Supaphol,Nujalee Dangseeyun,et al.Nonisothermal melt-crystallization kinetics for three linear aromatic polyesters.Thermochimica Acta,2003,406:207-220.
• [13]A Ziabicki.Fundamentals of fiber spinning[M].Wiley,NewYork:1976.112.
• [14]秦志忠,王希岳.改性PET非等温结晶行为的研究[J].合成纤维工业,1999,22(4):23.