姬洪,宋明根,薛勇,陈康,张玥,张玉梅
JI Hong,SONG Min-gen,XUE Yong,CHEN Kang,ZHANG Yue,ZHANG Yu-mei

• 1:东华大学纤维材料改性国家重点实验室
• 2:浙江尤夫高新纤维股份有限公司

摘要(Abstract)：

为了探究分子质量和共聚结构对阻燃共聚酯结晶动力学的影响,采用差示扫描量热仪对不同分子质量的阻燃共聚酯进行非等温结晶测试,并进行结晶动力学分析。结果表明:在聚酯中通过共聚反应引入共聚阻燃结构单元后,共聚酯的熔点降低,降温过程中的起始结晶温度和结晶峰温降低,分子质量较大的阻燃共聚酯的结晶温度有所下降,但这种影响并不明显;阻燃结构单元减少了可结晶的聚酯链段数量,结晶速率显著下降,且分子质量增大会造成链段活动能力降低,高分子质量的阻燃共聚酯的结晶速率大大降低。
In order to study the influence of molecular weight and copolymerization structure on the crystallization kinetics of flame retardant copolyester, the differential scanning calorimeter(DSC) was used to carry out non-isothermal crystallization test and crystallization kinetics for copolyester with different molecular weight. And the crystallization kinetics was analyzed according to the test results. The results showed that:after the introduction of copolymerization flame retardant structural units through copolymerization reaction,the melting point of copolyesters was lowered and in the cooling process the initial crystallization temperature and crystallization peak temperature decreased, and the crystallization temperature of the flame retardant copolyesters with larger molecular weight decreased, but this effect was not obvious. The number of crystallizable polyester chain segments was reduced by flame retardant structural units, and the crystallization rate was significantly slowed. Moreover, the increase of molecular weight would reduce the activity capacity of the chain segments and decrease the crystallization rate.

关键词(KeyWords)： 共聚酯;分子质量;阻燃;结晶动力学
copolyester;molecular weight;flame retardant;crystallization kinetics

Abstract:

Keywords:

基金项目(Foundation): 国家重点研发计划资助项目(2016YFB0303004);; 湖州市南太湖精英计划创新团队资助项目(2016HJYLB-03-B)

作者(Author): 姬洪,宋明根,薛勇,陈康,张玥,张玉梅
JI Hong,SONG Min-gen,XUE Yong,CHEN Kang,ZHANG Yue,ZHANG Yu-mei

DOI: 10.16090/j.cnki.hcxw.2021.01.001

参考文献(References)：

• [1]李允成.涤纶长丝生产(第二版)[M].中国纺织出版社,2002.
• [2]钱明球,刘兆峰,关桂荷.高模低缩涤纶工业丝的开发[J].产业用纺织品,1998(8):9-12.
• [3]BOURBIGOT S,DUQUESNE S.Fire retardant polymers:recent developments and opportunities[J].Journal of Materials Chemistry,2007,17(22):2283-2300.
• [4]王鸣义.高品质阻燃聚酯纤维及其织物的技术进展和趋势[J].纺织导报,2018(2):13-24.
• [5]陈咏,王颖,何峰,等.共聚型磷系阻燃聚酯聚合反应动力学及其性能[J].纺织学报,2019,40(10):13-18.
• [6]CHANG S,CHANG F.Synthesis and characterization of copolyesters containing the phosphorus linking pendent groups[J].Journal of Applied Polymer Science,1999,72(1):109-122.
• [7]赵雪,展义臻,何谨馨.涤纶无卤阻燃研究进展[J].染整技术,2008,30(12):12-16.
• [8]ASRAR J,BERGER P,HURLBUT J.Synthesis and characterization of a fire-retardant polyester:Copolymers of ethylene terephthalate and 2-carboxyethyl-(phenylphosphinic) acid[J].Journal of Polymer Science Part A Polymer Chemistry,1999,37(16):3119-3128.
• [9]WANG L,WANG X,YAN G.Synthesis,characterization and flame retardance behaviour of poly(ethylene terephthalate) copolymer containing triaryl phosphine oxide[J].Polymer Degradation and Stability,2000,69(1):127-130.
• [10]KOKKALAS D E,BIKIARIS D N,KARAYANNIDIS G P.Effect of the Sb2O3 catalyst on the solid-state polycondensation of poly(ethylene terephthalate)[J].Journal of Applied Polymer Science,2010,55(5):787-791.
• [11]王晓梅,袁宝庆.世界涤纶工业丝的发展趋势[J].中国橡胶,2004,20(23):7-9.
• [12]LI L J,DUAN R T,ZHANG J B,et al.Phosphorus-containing poly(ethylene terephthalate):solid-state polymerization and its sequential distribution[J].Industrial and Engineering Chemistry Research,2013,52(15):5326-5333.
• [13]JI H,GAN Y,KUMI A K,CHEN K,Z,et al.Kinetic study on the synergistic effect between molecular weight and phosphorus content of flame retardant copolyesters in solid-state polymerization[J].Journal of Applied Polymer Science,2020,137(38):49120.
• [14]马鹏程,王新东,庄源,等.阻燃涤纶工业丝的制备及性能研究[J].合成纤维,2015,44(12):14-17.
• [15]姬洪,张阳,陈康,等.基于动力学特性研究开发黑色高强聚酯工业丝[J].纺织学报,2020,41(4):1-8.
• [16]BALDENEGRO P L,NAVARRO R D,MEDELLIN R F,et al.Weight and Crystallization Temperature Effects on Poly(ethylene terephthalate)(PET) Homopolymers,an Isothermal Crystallization Analysis[J].Polymers,2014,6:583-600.
• [17]VAN A F,KREVELEN D W.Influence of crystallization temperature,molecular weight,and additives on the crystallization kinetics of poly(ethylene terephthalate)[J].Journal of Polymer Science Part B Polymer Physics,1972,10:2423-2435.
• [18]ZENDEHZABAN M,SHAMSIPUR M.Isothermal crystallization kinetics of poly(ethylene terephthalate)s of different molecular weights[J].Journal of the Iranian Chemical Society,2013,10:77-84.
• [19]王玉忠,吴大诚,郑长义.用DSC研究阻燃PET的结晶性和结晶动力学[J].高分子学报,1993(4):497-501.
• [20]刘海明,王锐,徐僖,等.新型阻燃剂-2-羧乙基苯基次膦酸及其阻燃共聚酯的制备、表征及热性能研究(英文)[J].材料工程,2009(S2):420-426.
• [21]高波,张培华.含磷阻燃共聚酯的合成、性能及其应用[J].聚酯工业,2001,14(3):11-13.
• [22]房长婧,梁倩倩,龚静华,等.磷系阻燃共聚酯纤维的微观结构与性能[J].合成纤维工业,2011,34(2):11-14.