李扬
LI Yang

• 1:陕西工业职业技术学院

摘要(Abstract)：

以XLA-棉包芯纱为经纱、纯棉纱为纬纱,在Y002S型小样织机上试织了4种XLA包芯纱-棉交织物,并测试了织物的断裂强力、断裂伸长率、耐磨性和褶皱回复性。测试结果表明:相同经纱密度下,斜纹组织织物的断裂强力和断裂伸长率大于平纹组织的;经纱密度越大,织物的耐磨性和褶皱回复性越好。
Using XLA-cotton core yarn as warp,cotton yarn as weft,four XLA-cotton interwoven fabrics are wovened in Y002 S sample loom,and the breaking strength,elongation at break,wear resistance and wrinkle recovery of the fabrics are tested.The test results show that at the same warp density,the breaking strength and elongation at break of twill weave fabric are higher than plain weave fabric,the warp density is higher,the wear resistance and wrinkle recovery are better.

关键词(KeyWords)： XLA包芯纱;棉纱线;交织物
XLA core yarn;cotton yarn;interwoven fabric