郭清华,蔡涛,张慧慧,邵惠丽,胡学超
GUO Qing-hua,CAI Tao,ZHANG Hui-hui,SHAO Hui-li,HU Xue-chao(State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

• 1:东华大学材料学院纤维材料改性国家重点实验室

摘要(Abstract)：

以1-乙基-3-甲基咪唑醋酸盐([EMIM] Ac)和1-丁基-3-甲基咪唑氯盐([BMIM] Cl)两种咪唑型离子液体为溶剂,研究比较了它们对纤维素的溶解性能及其溶液的纺丝加工性能。结果发现:两种离子液体均能在一定条件下溶解纤维素,但[EMIM] Ac较[BMIM] Cl对纤维素具有更低的溶解温度和更快的溶解速率。从流变分析还发现:纤维素/[EMIM] Ac溶液与纤维素/[BMIM] Cl溶液均为切力变稀流体,相同条件下纤维素/[EMIM] Ac溶液的黏度远低于纤维素/[BMIM] Cl溶液,使其可在相对低的温度下纺丝。此外,GPC分析结果表明:纤维素在用[EMIM] Ac溶解及纺丝过程中降解程度较小,而用[BMIM] Cl进行溶解纺丝时,降解作用则较明显。对纤维结构与力学性能的分析结果进一步表明:与相同喷头拉伸比下制得的[EMIM] Ac法再生纤维素纤维相比,[BMIM] Cl法再生纤维素纤维的聚集态结构相对较完善,结晶度与取向度更高些,从而使其力学性能也相对较好。
Two kinds of imidazole-based ionic liquids,1-ethyl-3-methylimidazolium acetate([EMIM]Ac) and 1-butyl-3-methylimidazolium chloride([BMIM]Cl) were used as the solvents of cellulose.The dissolution of cellulose in these two ionic liquids and the rheological behavior and spinning performance of the resultant dopes were investigated.It was found that cellulose had lower dissolution temperature and faster dissolution rate in [EMIM]Ac than in [BMIM]Cl.Both of cellulose/[EMIM]Ac and cellulose/[BMIM]Cl solutions were the typical shear thinning fluids.And the viscosity of the former was lower than that of the later,which means the cellulose/[EMIM]Ac solution could be spun under a lower temperature.GPC results showed further that during the dissolution and spinning process of cellulose,the degradation of cellulose was greater in [BMIM]Cl than that in [EMIM]Ac.Moreover,it was found that the orientation,crystallinity,breaking tenacity and initial modulus of the cellulose fiber regenerated from [BMIM]Cl were higher than those from [EMIM]Ac.

关键词(KeyWords)： 纤维素;离子液体;溶解;纤维
cellulose,ionic liquid,dissolution,fiber

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金项目(50873024);; 高等学校学科创新引智计划项目(No.111-2-04)

作者(Author): 郭清华,蔡涛,张慧慧,邵惠丽,胡学超
GUO Qing-hua,CAI Tao,ZHANG Hui-hui,SHAO Hui-li,HU Xue-chao(State Key Laboratory for Modification of Chemical Fibers and Polymer Materials

参考文献(References)：

• [1]宋俊,程博闻,丁长坤.离子液体-纤维素的新溶剂体系[J].人造纤维,2006,35(3):13-15,25.
• [2]Swatloski R P,Spear S K,et al.Dissolution of cellulose with ionic liquids[J].J Am Chem Soc,2002,124(18):4974-4975.
• [3]Laus G,Bentivoglio G,et al.Ionic liquids:Current developments,potential and drawbacks for industrial applications[J].Lenzinger Bericht,2005,84:71-85.
• [4]Hermanuta F,Gahr F,et al.New developments in dissolving and processing of cellulose in ionic liquids[J].Macromol Symp,2008,262:23-27.
• [5]任强,张军等.1-烯丙基-3-甲基咪唑室温离子液体的合成及其对纤维素溶解性能的初步研究[J].高分子学报,2003,(3):448-451.
• [6]Zhang H,Wu J,et al.1-Allyl-3-methylimidazolium chloride room temperature ionic liquid:a new and powerful nonderivatizing solvent for cellulose[J].Macromolecules,2005,38(20):8272-8277.
• [7]Heinze T,Schwikal K,Barthel S.Ionic liquids as reaction medium in cellulose functionalization[J].Macromolecular Bioscience,2005,5(6):520-525.
• [8]张慧慧,蔡涛等.以离子液体为溶剂的纤维素纤维的结构和性能[J].合成纤维,2007,36(11):11-15.
• [9]张慧慧,彭顺金等.用于制备高强Lyocell纤维的纤维素混合浆粕的研究[J].合成纤维,2007,36(1):21-24.
• [10]Bikova T,Treimanis A.Problems of the MWD analysis of cellulose by SEC using DMAc/LiCl:a review[J].Carbohydr Polym,2002,48:23-28.
• [11]Evans J M.Gel permeation chromatography:a guide to data interpretation[J].Polymer Engineering and Science,1973,13(6):401-408.
• [12]梁伯润,沈新元,王希岳等.高分子物理学[M].第二版.上海:中国纺织出版社,2003:82.
• [13]Oh S Y,Yoo D I,et al.Crystalline structure analysis of cellulose treated with sodium hydroxide and carbon dioxide by means of X-ray diffraction and FTIR spectroscopy[J].Carbohydrate Research,2005,340:2376-2391.
• [14]Northolt M G,Boerstoel H,Maatman H,et al.The structure and properties of cellulose fibers spun from an anisotropic phosphoric acid solution[J].Polymer,2001,42:8249-8264
• [15]程凌燕,朱天祥,刘崴崴等.纤维素在离子液体中的溶解特性研究[J].合成纤维,2008,37(4):9-13.