金盈,吴友吉,吴之传,雷小宝
JIN Ying, WU You-ji, WU Zhi-chuan, LEI Xiao-bao (Anhui University of Technology and Science

• 1:安徽工程科技学院

摘要(Abstract)：

以含偕胺肟基团的螯合纤维为原料,分别经Hg(NO3)2、Pb(NO3)2等溶液化学处理,制得五种不同类型的阴离子交换纤维。研究了时间、温度、pH值和离子浓度等因素对阴离子交换纤维吸附草酸根离子性能的影响。实验结果表明,汞阴离子交换纤维、铅阴离子交换纤维和铜阴离子交换纤维可以吸附草酸根离子,且汞阴离子交换纤维吸附性能最好。汞阴离子交换纤维在反应时间为90min、温度为40℃、pH值为9、草酸根离子浓度为0.05mol/L时,最高吸附量可达1.65mmol/g。
Five anion-exchange fibers were synthesized via chelate fiber with amidoxime group reacting with Hg (NO3)2, Pb (NO3)2 solution etc. The influences of the temperature, time, pH value and ion concentration on the adsorption properties of oxalate were determined. The results showed that Hg (II)- anion-exchange fiber, Pb(II)-anion-exchange fiber and Cu(II)-anion-exchange fiber could adsorb oxalate ion and Hg(II)-anion-exchange fiber was best. The highest adsorption capacity of Hg(II)-anion-exchange fiber was 1.65 mmol/g when the reaction temperature was 40 ℃, reaction time was 90 min, pH value was 9, and oxalate ion concentration was 0.05 mol/L.

关键词(KeyWords)： 阴离子交换纤维;草酸根离子;吸附
anion-exchange fiber, oxalate ion, adsorption

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金项目(20771002);; 安徽省教育厅高校青年基金资助项目(2007jq1085)

作者(Author): 金盈,吴友吉,吴之传,雷小宝
JIN Ying, WU You-ji, WU Zhi-chuan, LEI Xiao-bao (Anhui University of Technology and Science

参考文献(References)：

• [1]陈延林等.新型离子交换纤维的制备方法的探讨[J].高科技纤维与应用,2006(,4):25-28.
• [2]苏致兴.高分子螯合剂在分析化学中的应用[J].离子交换与吸附,1994,(5):453-455.
• [3]M R Lutfor,et al.Preparation and.characterization of(amidoxime)chelating resin from polyacrylonitrile grafted sago starch[J].European Polymer Journal,2000,36(10):2105-2113.
• [4]吕瑶姣等.螯合纤维的制备及其吸附重金属离子的研究[J].环境与开发,2001,(2):24-24.
• [5]吴之传等.改性聚丙烯腈纤维对铅镉汞离子的吸附性能的研究[J].水处理技术,2003,(4):92-5.
• [6]陶庭先等.阴离子交换纤维的制备及其对氟离子交换性能的影响的研究[J].合成纤维,2002,31(5):22-4.
• [7]沈敏等.壳聚糖分离富集-离子色谱法测定痕量草酸根[J].分析科学学报,2008,24(3):299-302.
• [8]陶庭先,吴之传等.螯合纤维的制备———聚丙烯腈纤维改性[J].合成纤维,2001,30(4):32-33.