浅谈碳纤维预浸料中铺放纤维非织造网布的适用性Discussion on the Applicability of Laying Open-Meshed Nonwovens in Carbon Fiber Prepreg
富儒年
FU Ru-nian
摘要(Abstract)：
选取了两种纤维非织造网布,分别在进口单向碳纤维预浸料和国产单向碳纤维预浸料层与层之间进行铺放,采用预浸料成型工艺制备不同性能的层合板,并通过测试层合板试样的力学性能和孔隙率,表明纤维非织造网布在碳纤维预浸料成型技术中的适用性。对比测试数据结果发现:纤维非织造网布经向纤维纤度、纬向纤维纤度、面密度选材合适时,在碳纤维预浸料层合板中表现出了优异的适用性;纤维非织造网布经向纤维纤度及纬向纤维纤度较小、面密度选择较大时,在碳纤维预浸料层合板中虽然也表现出良好的工艺适用性,但是碳纤维预浸料层合板的力学性能会降低,孔隙率会偏大。
Two kinds of open-meshed nonwovens were laid between the layers in the imported unidirectional carbon fiber prepreg and the domestic unidirectional carbon fiber prepreg. Prepreg molding process was used to prepare different properties laminates. The mechanical properties and porosity of the laminate indicated the applicability of the open-meshed nonwovens in the carbon fiber prepreg forming technology. According to the results of the test data, it shows that the open-meshed nonwovens exhibite excellent applicability in the carbon fiber prepreg laminate when the warp fineness, the weft fineness and the area density are selected to be properly. Although it also shows good process performance in carbon fiber prepreg laminates when the open-meshed nonwovens has a smaller selection of warp fineness, weft fineness, and a larger selection of area density, the mechanical properties of carbon fiber prepreg laminates are reduced and the porosity will be larger.
关键词(KeyWords)：
碳纤维预浸料;纤维非织造网布;工艺性能;力学性能
carbon fiber prepreg;open-meshed nonwoven;process performance;mechanical property
基金项目(Foundation):
作者(Author):
富儒年
FU Ru-nian
DOI: 10.16090/j.cnki.hcxw.2020.02.008
参考文献(References)：
- [1]潘翠红,孙占红.风电叶片用国产碳纤维预浸料的制备及性能研究[J].中国新技术新产品, 2017(12):147-148.
- [2]宋秋香,贾智源,高克强.风电叶片用国产碳纤维预浸料工艺性能和力学性能研究[J].玻璃钢/复合材料, 2016(2):40-46.
- [3]左洋,谢玉萍,孔静,等.碳纤维预浸料挥发分测试方法改进[J].化学分析计量, 2017, 26(1):105-108.
- [4]刘玲,路明坤,张博明,等.孔隙率对碳纤维复合材料超声衰减系数和力学性能的影响[J].复合材料学报, 2004(5):116-121.
- [5]褚国伟,张锦南,李海涛,等.风机叶片用单向碳纤维预浸料性能研究[J].玻璃钢/复合材料, 2012(4):87-90.