马帅,李好义,陈宏波,Mahmoud Bubakir,丁玉梅,杨卫民
MA Shuai,LI Hao-yi,CHEN Hong-bo,Mahmoud Bubakir,DING Yu-mei,YANG Wei-min

• 1:北京化工大学机电工程学院

摘要(Abstract)：

利用自制熔体微分静电纺丝装置探索聚丙烯(PP)分别与纳米碳酸钙(Ca CO3)、固体石蜡、混合无机盐3种不同共混体系的熔体电纺复合纤维的纺丝工艺,并利用后处理方法除去上述3种成孔剂,得到了表面粗糙并带有微孔的PP纤维。试验表明:在一定条件下,3种复合纤维均可由熔体微分电纺法制备,纤维平均直径分别为8.22、8.67和6.08μm,均小于纯PP纤维的12.10μm,纤维直径不随熔融指数增大而减小;气流辅助可以增加泰勒锥根数,当泰勒锥根数达到一定程度时,有助于射流的稳定和纤维的细化。3种复合纤维均可由后处理方法得到表面粗糙并带有微孔的结构:除去Ca CO3的纤维微孔大小不一,分布不均;除去固体石蜡的纤维表面粗糙,有条状和块状凹痕;除去无机盐的纤维微孔相对较小,分布较均匀。与纯PP纤维相比,3种复合纤维的直径更细,表面更粗糙,可以起到增强材料的亲水性(或疏水性)的作用。
In this study, polypropylene was mixed with three different pore-forming agents(nanometer cal-cium carbonate, paraffin and inorganic hybrid salts) to form three blended systems which were used to pro-duce composite fibers by self- made melt differential electrospinning device. Polypropylene fibers withrough surface and microporous were prepared after removing above-mentioned pore-forming agents. Thesurface morphological structures of these polypropylene fibers were characterized. Results showed that theaverage diameter of polypropylene-nanometer calcium carbonate composite fibers(8.22 μm), polypropylene-paraffin composite fibers(8.67 μm) and polypropylene-inorganic hybrid salts composites fiber(6.08 μm) wasless than pure polypropylene fibers(12.10 μm); the diameter of composite fibers was not reduced with theincreasing of melt index; polypropylene fibers without nanometer calcium carbonate comprised microporoushaving different sizes and uneven distribution, polypropylene fibers without paraffin had rough surface andstrip or bulk dents, polypropylene fibers without inorganic hybrid salts comprised microporous having rela-tively small sizes and even distribution. These three polypropylene fibers were all able to increase the hydro-philicity or hydrophobicity of materials. Furthermore, the number of Taylor cone was increased by using as-sistant air flow. Taylor cone contributed to the stability of jet flow and the refining of composite fibers whenTaylor cone increased to a certain number.

关键词(KeyWords)： 熔体微分静电纺丝;复合纤维;表面结构;成孔性
melt differential electrospinning,composite fiber,surface morphology,porosity

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金项目(21174015);; 北京市自然科学基金资助项目(2141002)

作者(Author): 马帅,李好义,陈宏波,Mahmoud Bubakir,丁玉梅,杨卫民
MA Shuai,LI Hao-yi,CHEN Hong-bo,Mahmoud Bubakir,DING Yu-mei,YANG Wei-min

DOI: 10.16090/j.cnki.hcxw.2014.12.010

参考文献(References)：

• [1]D W Hutmacher,P D Dalton,Melt electrospinning[J].Chem Asian J2011(6):44-56.
• [2]Zhou Y,Yang D Chen X,et al.Electrospun water-soluble carboxyethyl chitosan/poly(vinyl alcohol)nanofibrous membrane as potential wound dressing for skin regeneration[J].Biomacromolecules,2007,9(1):349-354.
• [3]徐勇,朱新声,高强,等.静电纺丝制备超细纤维复合材料[J].高分子材料科学与工程,2007,23(6):244-247.
• [4]Greiner A,Wendorff J H.Electrospinning:a fascinating method for the preparation of ultrathin fibers[J].Angewandte Chemie International Edition,2007,46(30):5 670-5 703.
• [5]Soliman S,Pagliari S,Rinaldi A,et al.Multiscale three-dimensional scaffolds for soft tissue engineering via multimodal electrospinning[J].Acta biomaterialia,2010,6(4):1 227-1 237.
• [6]Li X,Xie J,Yuan X,et al.Coating electrospun poly(ε-caprolactone)fibers with gelatin and calcium phosphate and their use as biomimetic scaffolds for bone tissuse engineering[J].Langmuir,2008,24(24):14 145-14 150.
• [7]Qi Z,Yu H,Chen Y,et al.Highly porous fibers prepared by electrospinning a ternary system of nonsolvent/solvent/poly(l-lactic acid)[J].Materials Letters,2009,63(3):415-418.
• [8]Lin Li,Raed Hashaikeh,Hassan A Arafat.Development of eco-efficient micro-porous membranes via electrospinning and annealing of poly(lactic acid)[J].Journal of Membrane Science,2013(436):57-67.
• [9]Megelski S,Stephens J S,Chase D B,et al.Micro-and nanostructured surface morphology on electrospun polymer fibers[J].Macromolecules,2002,35(22):8 456-8 466.
• [10]Kongkhlang T,Kotaki M,Kousaka Y,et al.Electrospun polyoxymethylene:Spinning conditions and its consequent nanoporous nanofiber[J].Macromolecules,2008,41(13):4 746-4 752.
• [11]Han S O,Son W K,Youk J H,et al.Ultrafine porous fibers electrospun from cellulose triacetate[J].Materials Letters,2005,59(24):2 998-3 001.
• [12]Diao Caihong,Xiao Changfa,Hu Xiaoyu,et al.Research of hydrophilic multi-porous polyacrylonitrile fiber and comfortability of its product[J].China Synthetic Fiber Industry,2010,33(4):28-31.
• [13]杨恩宁,郭静.Ca CO3/聚丙烯共混制备多孔聚丙烯纤维的研究[J].合成纤维,2006,35(2):25-27.
• [14]唐龙祥,严满清,刘春华,等.聚丙稀改性新进展[J].现代塑料加工应用,2002,14(6):36-39.
• [15]王全华.聚丙烯纤维的力学性能和耐老化性能的研究[D].北京:北京服装学院,2005:10-15.
• [16]扈景胜.聚丙烯纤维技术的最新进展[J].化学工程师,2005,114(3):42-44.
• [17]桑榆.产业用纺织品专用PP纤维[J].国际纺织学报,2006,34(2):4.
• [18]刘越.聚丙烯纤维在服装领域中的应用展望[J].山东纺织经济,2003(4):44-46.
• [19]Larrondo L,St John Manley R.Electrostatic fiber spinning from polymer melts.I.Experimental ob