孙海波,王双成,马军强,吕冬生,唐地源
SUN Hai-bo,WANG Shuang-cheng,MA Jun-qiang,Lü Dong-sheng,TANG Di-yuan

• 1:山东圣泉新材料股份有限公司

摘要(Abstract)：

腈纶本身的回潮率极低,容易产生静电。为了解决这个问题,采用分段浸渍法制备石墨烯导电腈纶,探讨了石墨烯导电腈纶的物理性能和导电性能。重点介绍了石墨烯导电腈纶的制备工艺流程,所采用的设备及腈纶的导电性能,并测试分析了石墨烯导电腈纶的摩擦性能、卷曲性能和力学性能。试验结果表明:石墨烯导电腈纶的比电阻由纯腈纶的1011Ω·cm变成106Ω·cm,抗静电效果得到明显改善;同时石墨烯导电腈纶的物理性能能够满足后道纺纱的要求,具有可纺性。
Due to the moisture regain of acrylic fiber is extremely low,it is easy to produce static electricity.To solve this problem,the graphene modified conductive acrylic fiber was prepared by piecewise impregnation method,and the physical property and conductivity of the modified acrylic fiber were investigated.The production process,the equipment,and the conductive of the acrylic fiber were focused on.The friction,crimp and mechanical properties of the modified acrylic fiber were also tested and analyzed.The experimental results show that the specific resistance of graphene modified conductive acrylic fiber is changed from 1011Ω·cm to 106Ω·cm,the antistatic effect has been improved obviously.At the same time,the physical properties of graphene modified acrylic fiber can meet the requirements of spinning process.

关键词(KeyWords)： 腈纶;石墨烯;导电纤维
acrylic fiber;grapheme;conductive fiber

Abstract:

Keywords:

基金项目(Foundation):

作者(Author): 孙海波,王双成,马军强,吕冬生,唐地源
SUN Hai-bo,WANG Shuang-cheng,MA Jun-qiang,Lü Dong-sheng,TANG Di-yuan

DOI: 10.16090/j.cnki.hcxw.2018.07.005

参考文献(References)：

• [1]张海霞,张喜昌.阻燃腈纶纤维性能与可纺性研究[J].棉纺织技术,2014,42(2):44-46.
• [2]孙海波,王双成,吕冬生,等.生物质石墨烯改性聚酰胺纤维的制备及性能表征[J].合成纤维,2017,46(7):14-16.
• [3]邬国铭,刘维锦,郭文霞,等.含五硫化九铜(Cu S)导电腈纶纤维的结构和性能[J].合成纤维工业,1995,18(3):11-16.
• [4]潘玮,黄素萍,龚静华.聚苯胺/涤纶导电纤维的制备及其织物抗静电性能研究[J].合成纤维,2002,31(1):30-32.