湿热处理对氨纶结构以及性能的影响Influence of Wet-Heat Treatment on Structure and Properties of Spandex
蒋曙,杨晓印,梁红军,毛兴树,陈厚翔
JIANG Shu,YANG Xiao-yin,LIANG Hong-jun,MAO Xing-shu,CHEN Hou-xiang
摘要(Abstract)：
使用恒温恒湿老化试验箱,研究了高温高湿环境下氨纶力学性能及微观结构的变化。通过傅里叶变换红外光谱、热力学分析仪、扫描电子显微镜及力学性能分析探究了氨纶湿热老化规律及机制,结果表明:在一定牵伸条件下,随湿度增加,氨纶丝内部氢键化程度变弱且湿度变化对氨纶的影响主要发生在硬链段区域;在高温环境下,氨纶的拉伸强力和拉伸伸长率比在低温环境下的低,而300%拉伸应力比在低温环境下的高,说明氨纶湿热老化本质是湿度对氨纶内部氢键化程度及水解的协同作用,而温度起到加速老化的作用。
Aging experiments of Spandex was carried out in constant humidity temperature test equipment, while the influence of humidity on structure and properties of Spandex under high temperature and high humidity was obtained with analysis of Fourier transform infrared spectroscopy, thermogravimetric analysis,scanning electron microscopy and mechanical properties. The results show that when Spandex is stretched to 300% elongation, with the increase of humidity, the degree of hydrogen bonding of Spandex becomes weak and the humidity has a significant effect on the hard segment of Spandex. At high temperature, the tensile strength and elongation ratio of Spandex are lower than those of low temperature environment, and the tensile stress ratio of 300% is higher than that of low temperature environment. This indicates that the wet-heat aging of Spandex is the synergistic effect of the degree of hydrogen bonding and hydrolysis, and temperature plays an accelerated role in aging.
关键词(KeyWords)：
氨纶;湿热老化;力学性能;氢键;热力学性能
Spandex;wet-heat aging;mechanical property;hydrogen bonding;thermodynamic property
基金项目(Foundation):
作者(Author):
蒋曙,杨晓印,梁红军,毛兴树,陈厚翔
JIANG Shu,YANG Xiao-yin,LIANG Hong-jun,MAO Xing-shu,CHEN Hou-xiang
DOI: 10.16090/j.cnki.hcxw.20190514.001
参考文献(References)：
- [1]肖泽润.基于结构与性能表征的氨纶老化行为研究[D].广州:华南理工大学,2016.
- [2]游革新,蔡斯迪,周序霖,等.聚氨酯纤维的紫外老化特性及分析[J].工程塑料应用,2017,45(9):93-98.
- [3]BOUBAKRI A,HADDAR N,ELLEUCH K,et al.Impact of aging conditions on mechanical properties of thermoplastic polyurethane[J].Materials&Design,2010,31(9):4194-4201.
- [4]周方颖,贺婕,余艳娥.碱处理对氨纶丝弹性力学性能的影响[J].上海纺织科技,2015,43(4):34-35.
- [5]陈海平,汪杰,涂根国,等.聚氨酯纤维的氯损研究[J].辽宁化工,2007,36(12):805-806.
- [6]蒋曙,张弈新,杨晓印,等.氨纶老化性能影响因素的研究进展[J].合成纤维,2018,47(11):4-7.
- [7]周方颖,张一心.碱,双氧水及热处理对氨纶丝力学性能的影响[J].丝绸,2014,51(6):11-15.
- [8]莫菲.熔纺氨纶织物湿热定型工艺及防脱散性能的研究[D].杭州:浙江理工大学,2016.
- [9]游革新,钟艳萍,肖泽润,等.高温高湿环境下紫外老化对氨纶结构及性能的影响[J].工程塑料应用,2018,46(5):23-27.
- [10]陈厚翔,梁红军,杨晓印,等.耐高温氨纶的结构与性能表征[J].合成纤维工业,2016,38(2):44-48.
- [11]左葆齐,朱俊芳.氨纶工艺热性能分析[J].苏州丝绸工学院学报,1997,17(4):10-16.
- [12]董进辉,阳建红,石增强,等.F-12纤维的湿热老化及拉伸性能[J].宇航材料工艺,2008,4:74-77.
- [13]赵若鹏,沈剑,徐时敏,等.耐热氨纶的研究现状[J].合成纤维工业,2012,34(5):38-41.
- [14]刘凉冰.四氢呋喃均聚醚聚氨酯弹性体(PTMG-PU)影响环境性能的因素[J].特种橡胶制品,2007,28(2):18-24.
- [15]江治,袁开军,李疏,等.聚氨酯的FTIR光谱与热分析研究[J].光谱学与光谱分析,2006,26(4):624-628
- [16]LIM LT,BRITT IJ,TUNG MA.Sorption and transport of water vapor in nylon 6,6 film[J].Journal of Applied Polymer Science,1999,71(2):197-206.