郑伟,邹黎明,徐速,倪建华
ZHENG Wei1, ZOU Li-ming2, XU Su1, NI Jian-hua2 (1. College of Material Science and Engineering

• 1:东华大学材料科学与工程学院
• 2:纤维材料改性国家重点实验室

摘要(Abstract)：

利用溶胶-凝胶法制备氮掺杂TiO2,并利用XRD、SEM、UV-Vis光谱和光催化降解实验对其进行结构性能表征。结果表明,经过氮掺杂的TiO2主要以锐钛矿晶型存在,并有极少量的金红石晶型存在;可见光响应性能比未掺杂的TiO2有很大的提高,其可见光响应范围在380～461nm之间;最终使其在可见光条件下对亚甲基蓝的降解活性得到显著增强,即光催化性能得到显著提高。
The N-doped TiO2 was prepared by sol-gel method, its structure and properties were studied by XRD, SEM, UV-Vis spectrum and test of photo -catalysis deterioration. The results indicated that N -doped TiO2 photo-catalyst was anatase crystalling phase with a small quantity of rutile crystalling phase. Its visible light absorptivity was better than no-doped TiO2, while the light absorb bound was from 380 nm to 461 nm. Its decomposed capability to the solution of methylene blue and photo-catalysis capability had greatly raised at visible light condition.

关键词(KeyWords)： 二氧化钛;光催化;溶胶-凝胶法;氮掺杂
titania, photo-catalyst, sol-gel method, N-doped

Abstract:

Keywords:

基金项目(Foundation): 上海市重点学科建设项目(编号B603)

作者(Author): 郑伟,邹黎明,徐速,倪建华
ZHENG Wei1, ZOU Li-ming2, XU Su1, NI Jian-hua2 (1. College of Material Science and Engineering

参考文献(References)：

• [1]冯彩霞.N掺杂纳米TiO2可见光催化氧化丙烯的动力学行为[J].物理化学学报,2008,24[4]:633-638.
• [2]胡红坡,赵宏生,郭子斌.氮掺杂TiO2光催化剂研究进展[J].材料导报,2008,2[22]:39-45.
• [3]Sun R D,Nakajima A,et al.Photo-induced surface nettability conversion of ZnO and TiO2thin films[J].Phys Chem B,2001,105[10]:1984-1990.
• [4]Akira Fujishima.Light-induced amphiphilic surfaces[J].Nature,1997,338[37]:431.
• [5]曹沛森.纳米TiO2光催化剂的改性及应用研究进展[J].纳米材料与结构,2008,3[45]:145-151.
• [6]Gyung Guk Kim,Joung Ah Kang.Photocatalytic degradation of volatile organics on TiO2embedded glass spherules[J].Catalysis Today,2007,129:96-101.
• [7]D S Tsoukleris,T Maggos.Surface modification of glass epoxy resin using the photocatalytic reaction in TiO2dispersed solution[J].Journal of Alloys and Compounds,2008,449:184-187.
• [8]郭文华,张军剑.溶胶-凝胶法及其制备纳米TiO2粉体的原理和研