竹纤维素在NMMO中溶解再生前后的结构研究Structural Characteristics of Bamboo Cellulose After Dissolution and Regeneration from N-Methylmorpholine-N-Oxide
黄锦锋
HUANG Jin-feng
摘要(Abstract)：
以竹浆粕为原料、N-甲基吗啉-N-氧化物(NMMO)为溶剂,利用傅里叶红外光谱、X射线衍射、热重分析等着重研究了竹纤维素在NMMO中溶解前后结构的变化。研究发现:NMMO溶解纤维素过程属于物理过程,未发生衍生化反应,竹纤维素溶解后聚合度较溶解前有所降低,晶型由纤维素Ⅰ变成了纤维素Ⅱ;热重分析表明纤维素再生前后都具有较好的热稳定性。
The bamboo pulp was chosen as the raw material of cellulose, and the regenerated cellulose fiber prepared by dissolving the bamboo cellulose in N-methylmorpholine-N-oxide(NMMO) solution. The structural differences between bamboo cellulose and regenerated cellulose fiber from NMMO had been investigated by using Fourier transform infrared spectroscopy, X-ray diffraction and TG analysis. The results show that NMMO dissolved cellulose is a physical process and no derivative reaction occurred after dissolution of bamboo cellulose, the degree of polymerization is lower than before dissolution, the crystalline form changed from cellulose Ⅰ to cellulose Ⅱ, and thermal weight analysis shows that cellulose has good thermal stability before and after regeneration.
关键词(KeyWords)：
NMMO;竹纤维素;溶解;再生
NMMO;bamboo cellulose;dissolve;regeneration
基金项目(Foundation):
作者(Author):
黄锦锋
HUANG Jin-feng
DOI: 10.16090/j.cnki.hcxw.20191205.001
参考文献(References)：
- [1] BIGANSKA Olga, NAVARD Patrick. Kinetics of precipitation of cellulose from cellulose-NMMO-water solutions[J]. Biomacromolecules, 2005(6):1948-1953.
- [2]冯坤. Lyocell竹纤维素纤维的研制[D].上海:东华大学, 2006.
- [3]王雪平.年产3万吨溶剂法纤维素纤维工业设计[D].济南:齐鲁工业大学, 2016.
- [4]谢飞,吕玲娟,李文江.芦苇纤维素在NMMO中的溶解及其再生前后性能的研究[J].膜科学与技术, 2015, 34(5):49-52.
- [5]贾向娟. NMMO/H2O溶液法制备高吸附再生纤维素材料的研究[D].西安:陕西科技大学, 2016.
- [6]李春花,徐纪刚,程春祖,等.纤维素浆粕在NMMO/H2O中的溶胀行为研究[J].纺织学报, 2014, 35(2):116-120.
- [7]刘晓辉,杨海茹,张慧慧,等. NMMO溶剂法纤维素海绵的制备及性能研究[J].合成技术与应用, 2014, 29(2):1-5.
- [8] PANDEY Ashok, SOCCOL Carlos R, NIGAM Poonam, et al. Biotechnological potential of agro-industrial residues.Ⅰ:cassava bagasse[J]. Bioresource Technology, 2000, 74(1):69-80.
- [9] PANDEY Ashok, SOCCOL Carlos R, NIGAM Poonam, et al. Biotechnological potential of agro-industrial residues. II:cassava bagasse[J]. Bioresource Technology, 2000, 74(1):81-87.
- [10] RICHARDSON S, GORTON L. Characterisation of the substituent distribution in starch and cellulose derivatives[J]. Analytica Chimica Acta, 2003, 497(1/2):27-65.
- [11]莫冬次. Lyocell纤维纺丝工艺概述[J].广西化纤通讯, 2002(1):25-29.
- [12]韩增强,武志云,汪少朋,等. Lyocen纤维纺丝溶剂NMMO及回收工艺的研究[J].山东纺织科技, 2007, 3:7-9.
- [13] LIU L f, WANG Q L, CHENG L D, et a1.Modification of natural bamboo fibers for textile applications[J]. Fibers and Polymers, 2011, 12(1):95.
- [14] SHI Yu, TIAN Chao, NI Jianping, et al. Study on improving the swelling performance of dissolving pulp in NMMO·H2O system[J]. China Pulp&Paper, 2018, 37(1):1-7.
- [15] NELSON M L, O'Connor R T. Relation of certain infrared bands to cellulose crystallinity and crystal latticetype. Part I. Spectra of lattice types,Ⅰ,Ⅱ,Ⅲand amorphous cellulose[J]. J Appl Polym Sci, 1964(8):1325-1341.
- [16]汤云潞,张慧慧,杨彦菊,等.纤维素浆粕性质对其在NMMO溶液中的溶胀性能的影响[J].合成纤维工业, 2018, 41(5):1-4.